this study investigates propagation of mode i crack in b70 pre-stressed concrete sleepers by fracture mechanics approach. a new experimental analysis is done for notched b70 pre-stressed concrete sleepers with replica test and image analysis. a scanning electron microscope test (sem) and an image analysis are applied for the replica test in order to determine crack length and crack mouth openin...

This study investigates propagation of mode I crack in B70 pre-stressed concrete sleepers by fracture mechanics approach. A new experimental analysis is done for notched B70 pre-stressed concrete sleepers with Replica test and image analysis. A scanning electron microscope test (SEM) and an image analysis are applied for the Replica test in order to determine crack length and crack mouth openin...

the cracked brazilian disc (cbd) specimen is widely used in order to determine mode-i/ii and mixed-mode fracture toughness of a rock medium. in this study, the stress intensity factor (sif) on the crack-tip in this specimen is calculated for various geometrical crack conditions using the extended-finite element method (x-fem). this method is based upon the finite element method (fem). in this m...

We monitored AEs during micro-indentation and pulse laser spallation test of CVD diamond film deposited on sintered SiC, and classified the fracture type by Lamb wave AE analysis. In the indentation test with a Rockwell sphere indenter, we observed Hertz ring cracks and simultaneously detected AEs from Mode-I fracture. Crack types were classified from polarity distribution of the first arrival ...

in this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. simulation results showed that mode i was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. afterward, the fract...

A nonlinear elastic foundation model has been developed to predict the mixed-mode (modes I and II) delamination failure of laminated composites. Two types of nonlinear elastic foundations were used to represent pure mode I and pure mode II components of the material failure ahead of the crack tip. One is a tension spring foundation for mode I component and the other is a shear spring foundation...