In this paper, the preparation process of low viscosity light curing silicon oxide ceramic slurry and properties sintered samples were studied. By studying effects type concentration dispersant solid content powder on stability slurry, with viscosity, high good was prepared. The ceramics verified by compressive strength, shrinkage test SEM observation. results show that stearic acid as dispersa...

This work presented a novel core-shell MnO2@m-SiO2 for catalyzing the removal of dyes from wastewater. MnO2 nanorods were sequentially coated with polydopamine (PDA) and polyethyleneimine (PEI) forming MnO2@PDA-PEI. By taking advantage of the positively charged amine groups, MnO2@PDA-PEI was further silicificated, forming MnO2@PDA-PEI-SiO2. After calcination, the composite MnO2@m-SiO2 was final...

Novel hierarchical Cd4SiS6/SiO2 based heterostructure nanowire arrays were fabricated on silicon substrates by a one-step thermal evaporation of CdS powder. The as-grown products were characterized using scanning electron microscopy, X-ray diffraction, and transmission electron microscopy. Studies reveal that a typical hierarchical Cd4SiS6/SiO2 heterostructure nanowire is composed of a single c...

Silicon dioxide (SiO2) nanoparticles (NPs) have been widely used in the biomedical field, such as in drug delivery and gene therapy. However, little is known about the biological effects and potential hazards of SiO2. Herein, the colloidal SiO2 NPs with two different sizes (20 nm and 100 nm) and different charges (L-arginine modified: SiO2 (EN20[R]), SiO2 (EN100[R]); and negative: SiO2 (EN20[-]...

Novel hierarchical Cd4SiS6/SiO2 based heterostructure nanowire arrays were fabricated on silicon substrates by a one-step thermal evaporation of CdS powder. The as-grown products were characterized using scanning electron microscopy, X-ray diffraction, and transmission electron microscopy. Studies reveal that a typical hierarchical Cd4SiS6/SiO2 heterostructure nanowire is composed of a single c...

The hollow CuO@SiO2 spheres with a mean diameter of 240 nm and a thin shell layer of about 30 nm in thickness was synthesized using an inorganic SiO2 shell coating on the surface of Cu@C composite that was prepared by a two-step hydrothermal method. The obtained hollow CuO@SiO2 spheres were characterized by ICP-AES, nitrogen adsorption-desorption, SEM, TEM, XRD, H2-TPR, CO-TPR, CO-TPD and NO-TP...

The interaction of hydrogen with Pd-SiO2 interfaces has been investigated for the first time using first-principles calculations based on density functional theory. The hydrogen-induced polarization at the Pd-SiO2 interfaces was evaluated using Pd-SiO2 interface supercells. As a result, the potential change induced by interfacial hydrogen atoms was not observed even for hydrogen concentration o...