The arc thermal metal spraying method (ATMSM) provides proven long-term protective coating systems using zinc, aluminum and their alloys for steel work in a marine environment. This paper focuses on studying experimentally the anti-corrosion criteria of ATMSM on steel specimens. The effects of the types of spraying metal and the presence or absence of sealing treatment from the thermal spraying...

The present study is an attempt to find out the effect of environmental corrosion on the commonly used pearlitic rail steel. The cases of corrosion of rail under Indian environment have been studied. It has been found that in marine environment both the yield strength and tensile strength decreases with increasing corrosion rate. In acidic environment yield strength increased with increasing co...

Corrosion of steel reinforcement is the major cause of deterioration in concrete structures, and carbon dioxide and especially chlorides are the main causes of damage. The rate at which chloride ions diffuse through concrete is a major determinant of the durability of structures. If chloride ions reach the vicinity of the rebar, the passive film around the steel can start to break down and the ...

in this research, mesoporous silica was applied as the host of corrosion inhibitor (molybdate). the loaded mesoporous silica was dispersed in an epoxy matrix. the composite was then coated on the mild steel plate. results showed that the corrosion resistance of the scratched epoxy/mesoporous silica loaded by molybdate was better than the one without molybdate or neat epoxy. on the other hand, e...

Reinforcing steel embedded in fresh concrete develops a protective passive layer on its surface. This layer, which is formed as result of high alkalinity of the concrete pore solution (pH~13), consists of γ-Fe2O3 adhering tightly to the steel. As long as that oxide film is present, the steel remains intact [1]. However, chloride ions attack and concrete carbonation can destroy the film and, in ...

Mild Steel and their products are main raw material for a strong infrastructure for every country which is the main demand in the race of survival, stabilization, growth and competition for every country. Industrialization and modernization in now a days has made a strong demand of steel and their maintenance but atmospheric corrosion can aggressively accelerate the degradation of metals during...

In this paper, a new kind of carbon steel (CS) and stainless steel (SS) galvanic sensor system was developed for the study of rebar corrosion in different pore solution conditions. Through the special design of the CS and SS electronic coupons, the electronic resistance (ER) method and zero resistance ammeter (ZRA) technique were used simultaneously for the measurement of both the galvanic curr...

In this paper, the corrosion resistance of laser-welded composite arch wire (CoAW) with Cu interlayer between NiTi shape memory alloy and stainless steel wire in artificial saliva with different concentrations of protein was studied. It was found that protein addition had a significant influence on the corrosion behavior of CoAW. Low concentration of protein caused the corrosion resistance of C...

Corrosion is one of the major problems in the industry especially on machinery since it weakens the structure of the machinery part and causes the mechanical failure. This will stop the production and increase the maintenance cost. In this study, the corrosion behaviour of gas nitriding on a screw press machine shaft made from AISI 4140 steel was investigated. Pitting corrosion was identified a...

The role of salivary media is essential during mastication and ingestion processes; yet it can hinder the performance of foreign materials in the oral cavity. The aim of this study was to examine the effects of applied load and applied electrical potential on the tribo-corrosion mechanisms of 316L stainless steel in an environment similar to oral cavity conditions. 316L stainless steel is a mat...