Several formulations of alternative alloys have been proposed for the substitution of gold-based alloys used in Dentistry. Recently, a Ni-Cr-Ti-based alloy has been introduced. The purpose of this work was to verify the marginal adaptation obtained with one-piece superstructures for implant-supported prostheses obtained in Ni-Cr-Ti alloy, compared to a semi-noble alloy Pd-Ag. Eight superstructu...

In AA2618 aluminum alloy, the iron- and nickel-rich intermetallics formed during solidification are of great effect on the mechanical properties of the alloy at both room temperature and elevated temperatures. However, the solidification behavior of the alloy and the formation mechanism of the intermetallics during solidification of the alloy are not clear. This research fills the gap and contr...

OBJECTIVE To evaluate the effects of recasting on the biocompatibility of a commercially available Ni-Cr alloy. METHODS The alloy tested was cast and subsequently recast four more times. For each cast condition, 24 disk shaped specimens were fabricated (5 mm in diameter, 0.5 mm in thickness). All the recasting was performed without adding new alloy. After the first cast and following each rec...

Chemical syntheses of homogenous solid solution alloy nanoparticles of noble metals require high temperature above 100 °C. Beside this, aqueous co-reduction methods lead to phase separation. In contrast, pulsed laser ablation in liquid (PLAL) allows synthesis of alloy nanoparticles with totally homogeneous ultrastructure in aqueous media at room temperature without reducing agents or organic li...

Commercial Ag-based alloy (46Ag-20Pd-12Au-20Cu alloy) is widely used in Japan as a casting alloy. As opposed to the commercial composition, we prepared five experimental Ag-based alloys with reduced Pd content of 10 or 12%, increased Au content of 20 to 30%, and reduced Cu content of 12 to 20%. We then evaluated their sulfuration resistance by analyzing cast specimen surfaces dipped in 0.1% Na2...

A low magnetic Zr-1Mo alloy was fabricated by a powder bed fusion (PBF) process using a fiber laser. The microstructure, surface morphology, and pore distribution of the as-built Zr-1Mo alloy were observed. Its magnetic susceptibility and Vickers hardness were evaluated by magnetic susceptibility balance and a microindentation tester, respectively. The as-built Zr-1Mo alloy mainly consisted of ...

This study investigates the effects of niobium and molybdenum on FeCoNi alloy, including on the microstructures and hardness of FeCoNiNb0.5Mo0.5 and FeCoNiNb alloys, and the polarization behaviors of these alloys in 1 M sulfuric acid and 1 M sodium chloride solutions. The results in this study indicate that both FeCoNiNb0.5Mo0.5 and FeCoNiNb alloys had a dual-phased dendritic microstructure; al...

The influence of zirconium on the grain refinement of Al 6063 alloy has been experimentally investigated. The microstructure and macrostructure of the refined alloy were investigated. The experimental results reveal that, the coarse dendrites in the microstructure of the alloy are effectively refined with the addition of zirconium to the melt prior to solidification. Grains of Al 6063 alloy can...

The density and the specific heat of liquid Au–Cu alloy above and below the melting temperature are investigated in a wide composition range via constant temperature and constant pressure molecular dynamics simulations. The atomic interaction of the alloy is described with the embedded-atom method (EAM). The equilibrium melting temperature is evaluated from the change in the growth direction of...

The amorphous ternary metallic alloy Zr60Al15Ni25 was oxidized in dry oxygen in the temperature range 310 ±C to 410 ±C. Rutherford backscattering (RBS) and cross-sectional transmission electron microscopy (TEM) studies suggest that during this treatment an amorphous layer of zirconium-aluminum-oxide is formed at the surface. Nickel was depleted in the oxide and enriched in the amorphous alloy n...