There are two well-known phenomena associated with the bainite reaction, both of which have been exploited here to enhance the mechanical behaviour of steel. Firstly, the bainite plate size decreases as the transformation temperature is reduced. Secondly, it is bad to have large regions of untransformed austenite in the microstructure; this is because they can transform, under the influence of ...

The effects of increasing nickel from 3 to 7 and 9 wt. % were investigated in high strength steel weld metals with 2 wt. % manganese. It was found that nickel additions were positive for strength but negative for impact toughness. Significant segregation of nickel and manganese to interdendritic regions was observed with the two higher nickel contents. In these weld metals a mainly martensitic ...

The different techniques available for the accurate measurement of lattice fringe spacings are discussed and their relative merit under different circumstances assessed. The relationship between the lattice fringe spacing and the lattice parameter is further examined for both uniform and chemically inhomogeneous material. The techniques described were also applied to an investigation of carbon ...

The kinetics and mechanism of bainite transformation have been studied in Fe-Cr-Mo-V-Ti-C steel high speed dilatometry backed by thermodynamic analysis. The complete transformation of austenite, however, has not occurred at any reported temperature. Obtained results confirm the incomplete reaction phenomenon with the cessation of the bainite transformation well before the paraequilibrium is ach...

With careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thin films of stable retained austenite have exhibited impressive combinations of strength and toughness in highsilicon bainitic steels. The silicon suppresses the precipitation of brittle cementite leading to an improvement in toughness. The essential principles governing the optimisatio...

Duplex stainless steel multi-pass welds were made at 0.15 MPa, 0.45 MPa, and 0.75 MPa pressure, simulating underwater dry hyperbaric welding by the flux-cored arc welding (FCAW) method, with welds of normal pressure as a benchmark. The purpose of this work was to estimate the effect of ambient pressure on the microstructure, pitting corrosion resistance and impact toughness of the weld metal. T...

We perform density-functional theory ~DFT! calculations of carbon dissolution and diffusion in iron, the latter being a typical example of interstitial diffusion. The Kohn-Sham equations are solved with periodic boundary conditions and within the projector-augmented-wave formalism, using the generalized gradient approximation for electron exchange and correlation. With the solution enthalpy as ...

To investigate the effect of tempering treatment on mechanical properties and the microstructure of DIN 1.4021 Martensitic Stainless Steel, austenite treatment was conducted for the samples at 1000 ºC temperature for 60 min and then the samples were oil quenched. Later, tempering treatments were performed for the samples at 500 ºC and 700 ºC temperatures for 2 and 5 h, respectively; then quench...