In this work, the results obtained from studying the corrosion of cast iron in freely aerated stagnant Arabian Gulf seawater (AGS) at room temperature were reported. The study was carried out using weight-loss (WL), cyclic potentiodynamic polarization (CPP), open-circuit potential (OCP), and electrochemical impedance spectroscopy (EIS) measurements and complemented by scanning electron microsco...

For an efficient high-temperature reversible solid oxide fuel cell (RSOFC), the oxygen electrode should be highly active for the conversion between oxygen anions and oxygen gas. CaMnO(3-δ) (CM) is a perovskite that can be readily reduced with the formation of Mn(3+) giving rise to oxygen defective phases. CM is examined here as the oxygen electrode for a RSOFC. CaMn(0.9)Nb(0.1)O(3-δ) (CMN) with...

Diminishing surface wettability is an effective method to improve corrosion resistance of aluminum. Various techniques for preparing hydrophobic surface have been reported, most of which use organic coating as the final step. The key point to diminish surface wettability is to form a fine regular surface structure, and the porous type anodic oxide film (PAOF) has nano-pore structure, therefore ...

Among the various causes of free chlorine consumption in drinking water distribution networks, the internal corrosion of pipes has not been so far seriously considered. This work focused on the corrosion study of cast iron, as a representative material of those networks, in non-chlorinated and chlorinated waters, by both electrochemical impedance spectroscopy and classical photographic observat...

Ž . The anodic polarization process in metal-hydride electrodes occurs via the following consecutive steps: i diffusion of absorbed Ž . hydrogen from the bulk to the surface of the electrode, ii hydrogen transfer from absorbed state to adsorbed state at the electrode Ž . surface, and iii electrochemical oxidation of the adsorbed hydrogen on the electrode surface. A theoretical treatment is pres...

Corrosion resistance of AA1070 aluminum alloy (AA1070) was compared to reinforced with alumina at weight composition (wt. %) 5% and 10%, grain size 150 nm 600 nm. Potentiodynamic polarization open circuit potential analysis were employed in 0.0125 M H2SO4, 3.5% NaCl H2SO4-3.5% solutions. Data showed solution the most deleterious peak corrosion rate value 6.682 mm/y while weakest 0.084 mm/y. wt....

Potentiodynamic polarization and impedance tests were carried out on 316L stainless steel with culturing murine fibroblast L929 cells to elucidate the corrosion behaviour of 316L steel with L929 cells and to understand the electrochemical interface between 316L steel and cells, respectively. Potential step test was carried out on 316L steel with type I collagen coating and culturing L929 cells ...

Anode biofilm is a crucial component in microbial fuel cells (MFCs) for electrogenesis. Better knowledge about the biofilm development process on electrode surface is believed to improve MFC performance. In this study, double-chamber microbial fuel cell was operated with diluted POME (initial COD = 1,000 mg L(-1)) and polyacrylonitrile carbon felt was used as electrode. The maximum power densit...

A thin silver chloride layer deposited on a conducting support photocatalyzes the oxidation of water to O(2) in the presence of a small excess of silver ions in solution. The light sensitivity in the visible part of the spectrum is due to self-sensitization caused by reduced silver species. Anodic polarization reoxidizes the reduced silver species. To test its water splitting capability, AgCl p...

The corrosion inhibition of mild steel in 1 M HCl solution by some dihydropyridine has been studied using gravimetric, electrochemical impedance spectroscopy, potentiodynamic polarization techniques and quantum chemical study. results weight loss Tafel measurements showed that among the compounds, Isradipine good inhibiting properties for acidic bath, with 98% efficiency at optimum concentratio...