introduction: the aim of this study was to evaluate the compressive strength of calcium-enriched mixture (cem) cement in contact with acidic, neutral and alkaline ph values. methods and materials: the cement was mixed according to the manufacturer’s instructions, it was then condensed into fourteen split molds with five 4×6 mm holes. the specimens were randomly divided into 7 groups ( n =10) an...

introduction: the provision of an effective apical seal is an essential factor when choosing an appropriate material for success of root-end surgeries. root-end resection, preparation and obturation should provide an adequate apical seal. the aim of this in vitro study was to investigate bacterial and dye microleakage of four different root-end filling materials and compare the efficacy of thes...

Crown fractures account for the majority of dental traumas. If handled properly, prognosis of the pulp following a traumatic crown fracture can be favorable. The present case report focuses on the treatment of a traumatized mature permanent incisor with exposed pulp that was treated with the novel technique of miniature pulpotomy using calcium-enriched mixture (CEM) cement. One-year follow-up r...

Introduction: The aim of this study was to assess the fracture strength of immature single-rooted teeth restored with fiber post and apical plug. Materials &Methods: In this experimental study, fifty mandibular premolars were divided into five groups. The coronal and apical portions were cut to obtain15±1 mm root lengths and cleaning &shaping were performed. Peeso reamer #4 was passed t...

introduction: the aim of this study was to compare the discoloration potential of calcium-enriched mixture (cem) cement, white mineral trioxide aggregate (wmta) and calcium hydroxide (ch), after placement in pulp chamber. methods and materials: access cavities were prepared in 40 intact maxillary central incisors. then, a 2×2 mm box was prepared on the middle third of the inner surface on the b...

introduction: the aim of this in vitro study was to determine the sealing ability of orthograde proroot mineral trioxide aggregate (mta) and calcium enriched mixture (cem) cement as root-end filling materials. materials and methods: fifty four extracted single-rooted human teeth were used. the samples were randomly divided into 3 experimental groups. in group a and b, 4 mm of wmta and cem cemen...

introduction: the purpose of this study was to evaluate the effect of different solvents; carbonic acid (h 2 co 3 ), hydrochloric acid (hcl), chlorhexidine (chx) and sodium hypochlorite (naocl) on the surface hardness of mineral trioxide aggregate (mta) and calcium-enriched mixture (cem) cement. methods and materials: plexiglass molds were prepared and filled with angelus mta or cem cement and ...

Water tightness of a concrete cover layer is important, as it is typically used as a protective coating of the steel reinforcement. Water tightness can be impaired by crack formation or by permeability. A bacteria-based lactate-derived healing agent (HA) can be added to concrete to enhance the potential for restoration of water tightness. Bacterial conversion of the included carbon source resul...

The aim of this study was to evaluate the cytotoxicity of three types of calcium silicate-based endodontic cement after different incubation periods with human periodontal ligament fibroblasts. Human periodontal ligament fibroblasts were cultured from extracted third molars and seeded in 96-well plates. MTA, calcium enriched mixture (CEM) cement, and Biodentine were prepared and added to cultur...

OBJECTIVE This study was aimed to evaluate and to compare the push-out bond strength of different brands of mineral trioxide aggregate (MTA) with a calcium enriched mixture cement (CEM). MATERIALS AND METHODS Fifteen extracted, single-rooted human teeth were used. The middle-third of the roots were sliced perpendicular to the long axis into 1.00 ± 0.05 mm thick serial slices (15 root × 4 slic...