To investigate the gradual failure of high-density polyethylene (HDPE) geomembrane as a result of long-term corrosion, four dynamic corrosion tests were conducted at different temperatures and durations. By combining tension and puncture tests, we systematically studied the variation law of tension and puncture properties of the HDPE geomembrane under different corrosion conditions. Results sho...

Protective coating corrosion failure is a complicated process that involves various phenomena which are hard to test for separately. An adequately protected pipe can be in service for a relatively long time without exhibiting any signs of corrosion failure, and then all of a sudden it corrodes over a short period of time. Failure will definitely happen if the interface between the pipe surface ...

Corrosion associated with microorganisms has been recognized for over 50 years and yet the study of microbiologically influenced corrosion (MIC) is relatively new. MIC can occur in diverse environments and is not limited to aqueous corrosion under submerged conditions, but also takes place in humid atmospheres. Biofouling of industrial water systems is the phenomenon whereby surfaces in contact...

continue on reverse if necessary and identify by block number) The corrosion mechanisms and behavior of a P-130x graphite fiber reinforced 6063 aluminum composite laminate were udied. Electrochemical and total immersion tests were performed on the composite in 3.5% sodium chloride and 5.0% >dium sulfate solutions. The effects of pH, the presence of sulfite ions, various heat treatments, and ele...

Eight retrieved metal-on-metal total hip replacements displayed corrosion damage along the cobalt-chromium alloy liner taper junction with the Ti alloy acetabular shell. Scanning electron microscopy indicated the primary mechanism of corrosion to be grain boundary and associated crevice corrosion, which was likely accelerated through mechanical micromotion and galvanic corrosion resulting from ...

In this paper, the corrosion residual strength of the AZ91D magnesium alloy in the presence of sulfate-reducing bacteria is studied. In the experiments, the chemical composition of corrosion film was analyzed by a scanning electron microscope with energy dispersive X-ray spectroscopy. In addition, a series of instruments, such as scanning electronic microscope, pH-meter and an AG-10TA materials...

Corrosion is a significant maintenance problem, especially for aging aircrafts, with the Air Force recently estimating corrosion maintenance costs exceeding $800M per year. Nondestructive evaluation (NDE) techniques can be used to detect corrosion under paint and hidden within layered structures. However, it is difficult to capture a comprehensive picture of the corrosion environment using any ...

Because of the existence of corrosion media such as chlorine, serious corrosion attacks ships, offshore and marine structure. Scholars worldwide have been long committed to the research of marine corrosion and development of anti-corrosion agents, and have achieved remarkable results. But so far, the conventional ocean coating inevitably makes microholes or microcracks between the additive and ...

A review is provided about the current research on magnesium/magnesium alloys corrosion in the industry. Except for reviewing the kinds of corrosion on galvanic corrosion, stress corrosion, and corrosion fatigue, its corresponding mechanisms are also explained, such as the influence of metallurgical factors, and environmental factors. Furthermore, the protection of magnesium/magnesium alloys co...

The increase in CO2 concentrations and global warming will increase the carbonation depth of concrete. Furthermore, temperature rise will increase the rate of corrosion of steel rebar after carbonation. On the other hand, compared with normal concrete, high volume fly ash (HVFA) concrete is more vulnerable to carbonation-induced corrosion. Carbonation durability design with climate change is cr...