Current studies on the fatigue lifetime of ceramics are mostly focused on the relation between the stress amplitude (or maximum stress) and cycles to failure. For a more compliant and plastic ceramic which has a pronounced nonlinear stress-strain relation, the role of plastic strain in the fatigue damage is investigated for the first time in this study using a 12 mol% Ce-TZP. By testing at diff...

It is well known that mechanical surface treatments, such as deep rolling, shot peening and laser shock peening, can significantly improve the fatigue behavior of highly-stressed metallic components. Deep rolling (DR) is particularly attractive since it is possible to generate, near the surface, deep compressive residual stresses and work hardened layers while retaining a relatively smooth surf...

The high-cycle, push-pull fatigue fracture behavior of high-C, Si-Al-rich nanostructured bainitic steel was studied through the measurement of fatigue limits, a morphology examination and phase composition analysis of the fatigue fracture surface, as well as fractography of the fatigue crack propagation. The results demonstrated that the push-pull fatigue limits at 10⁷ cycles were estimated as ...

Bulk silicon is not susceptible to high-cycle fatigue but micron-scale silicon films are. Using polysilicon resonators to determine stress-lifetime fatigue behavior in several environments, oxide layers are found to show up to four-fold thickening after cycling, which is not seen after monotonic loading or after cycling in vacuo.We believe that the mechanism of thin-film silicon fatigue is ‘‘re...

Fatigue is the primary cause of failure of crankshafts in internal combustion engines. The cyclic loading conditions and the stress concentrations in the crank pin fillets are unavoidable, and can result in fatigue failure. The objectives of this study were to compare the fatigue behavior of forged steel and ductile iron crankshafts from a one-cylinder engine as well as to determine if the fati...

This experimental study investigated the effects of quenching and tempering heat treatment on fatigue behavior and also tempering temperature and time holding of AISI 1060 steel. At first, the specimens were austenitized at 800˚C for 1 hour, and then were quenched in the water bath of 25˚C temperature. After that, tempering process was done at the temperature of 250˚C, 450˚C and 650˚C for 1 and...

Fatigue failure in micron-scale polycrystalline silicon structural films, a phenomenon that is not observed in bulk silicon, can severely impact the durability and reliability of microelectromechanical system devices. Despite several studies on the very high-cycle fatigue behavior of these films !up to 1012 cycles", there is still an on-going debate on the precise mechanisms involved. We show h...