CONTEXT Resin luting of all-ceramic restorations results in increased performance; however, the strengthening mechanism and the role of the mechanical properties of the resin are not fully understood. OBJECTIVE The aim of this study was to investigate the effect of filler content on the flexural properties of resin luting agents and thereby selecting an appropriate resin luting cement. MATE...

fiber reinforced concrete (frc) has been widely used due to its advantages over plain concrete such as high energy absorption, post cracking behaviour, flexural and impact strength and arresting shrinkage cracks. but there is a weak zone between fibers and paste in fiber reinforced concretes and this weak zone is full of porosity, especially in hybrid fiber reinforced concretes. so it is necess...

In this paper the effect of hardener on mechanical properties of carbon reinforced phenolic resin composites is investigated. Carbon fibre is one of the most useful reinforcement materials in composites, its major use being the manufacture of components in the aerospace, automotive, and leisure industries. In this study, carbon fibres are hot pressed with phenolic resin with various percentages...

UNLABELLED PUORPOSE: The aim of this study was to evaluate the effect of specimen dimensions on the flexural strength of a composite resin (Heliomolar RO). METHODS The different dimensions tested - length x width x height (mm) were: 25x2x4; 25x2x2 (ISO 4049); 15x2x2; 10x2x2 and 10x2x1. Light-curing was performed at 600 mW/cm² for 40s, three times along the 25mm specimens, twice along 15mm spe...

In this study, we determined the flexural properties and tensile shear strength of five-ply plywood panels produced with eucalyptus (Eucalyptus grandis), beech (Fagus orientalis), and hybrid poplar (Populus x euramericana) using urea-formaldehyde (UF), melamine-urea-formaldehyde (MUF) and phenol-formaldehyde (PF) adhesives. Flexural properties were tested on both parallel and perpendicular to g...

In the present study, effect of pozzolanic material (Metakaolin and Silica fume) is studied through compressive and Flexural strength in cement concrete. Metakaolin and silica fume area used as cement replacement materials at 5%, 10% and 15% by mass keeping water–cement ratio as 0.42 Compressive and Flexural strength were observed after 7 and 28 days of curing. Silica fume is a by products resu...

In the present study, the mechanical properties of self-compacting concrete were investigated after the addition of different amounts of ZnO nanoparticles. The zinc oxide nanoparticles, with an average particle size of about 30 nm, were synthesized and their properties studied with the help of a scanning electron microscope (SEM) and X-ray diffraction. The prepared nanoparticles were partially ...

A nanocomposite containing polypropylene (PP) and nano α-Al2O3 particles was prepared using a Haake internal mixer. Mechanical tests, such as tensile and flexural tests, showed that mechanical properties of the composite were enhanced by addition of nano α-Al2O3 particles and dispersant agent to the polymer. Tensile strength was approximately ∼ 16% higher than pure PP by increasing the nano α-A...

490 MRS BULLETIN/JULY 2002 nated by intergranular fracture, while in AJM it was in a manner resembling ductile behavior. Improved surface finishing by AJM resulted in a 15% improvement in flexural strength, compared with both ground and ground-plus-lapped samples. The researchers concluded that a higher compressive residual stress observed on the AJM-processed surface, combined with the smoothe...