in the present study, the effect of various weight fractions of graphene nanoplatelet (gpl) on flexural fatigue behavior of epoxy polymer has been investigated at room temperature and generally the temperature was monitored on the surface of specimen during each test. the flexural stiffness of grapheme nano-platelet/epoxy nanocomposites at 0.1, 0.25 and 0.5 wt. % as a main effective parameter o...

This study investigated the influence of porosity on the flexural property of a nanoporous alumina film. When the porosity of the alumina film increased, both bending strength and modulus declined. The results from the bending test revealed that the setting of the film during the bending test had significant influence on the flexural property. Fracture only occurred when the porous side of the ...

Traditional interfacial toughness measurements for thin films on substrate are not appropriate to the structure composed of stiff films and soft substrate. This paper describes a new bending test system to measure the interfacial toughness for the soft interface between stiff films and elastomeric substrate. The experimental setup including the loading stages is easy to operate and scanning ele...

The fracture strength of ZnO nanowires vertically grown on sapphire substrates was measured in tensile and bending experiments. Nanowires with diameters between 60 and 310 nm and a typical length of 2 μm were manipulated with an atomic force microscopy tip mounted on a nanomanipulator inside a scanning electron microscope. The fracture strain of (7.7 ± 0.8)% measured in the bending test was fou...

In this research, using the Modified Compression Field Theory (MCFT), a new model is proposed to predict the behavior of reinforced concrete coupling beams. The model is able to consider the effects of shear and axial forces and bending moment, simultaneously. The proposed model includes a nonlinear shear spring, an axial spring and some nonlinear springs for considering bending deformations. I...

This study evaluated the effect of water-bath and microwave post-polymerization treatments on the flexural strength and Vickers hardness of four autopolymerizing reline resins (Duraliner II-D, Kooliner-K, Tokuso Rebase Fast-TR and Ufi Gel Hard C-UGH) and one heat-polymerized acrylic resin (Lucitone 550-L), processed using two polymerization cycles (short cycle - 90 minutes at 73 degrees C and 1...

The direct Itype transitions of H l 3 C , 4 N l 6 0 in the vibrational states ( i^ i ' s ) = (01) and (03) were measured in the frequency range from 18 to 40 GHz. These transitions show a nuclear quadrupole hyperfine structure caused by the l 4 N nucleus, which could partially be resolved at Doppler-limited resolution. The analogous transitions of the parent species. H l 2 C l 4 N 1 6 0 , were ...