Lead zirconate titanate (Pb(1.1)(Zr(0.52)Ti(0.48))O(3)) thin films of thickness 260 nm on Pt/Ti/SiO(2)/Si substrates were densified by 2.45 GHz microwave annealing. The PZT thin films were annealed at various annealing temperatures from 400 to 700 °C for 30 min. X-ray diffraction showed that the pyrochlore phase was transformed to the perovskite phase at 450 °C and the film was fully crystalliz...

We demonstrate a pyroelectric nanogenerator (PENG) based on a lead zirconate titanate (PZT) film, which has a pyroelectric coefficient of about -80 nC/cm(2)K. For a temperature change of 45 K at a rate of 0.2 K/s, the output open-circuit voltage and short-circuit current density of the PENG reached 22 V and 171 nA/cm(2), respectively, corresponding to a maximum power density of 0.215 mW/cm(3). ...

Multiferroics are currently intensely investigated because the coexistence and coupling of ferroic arrangements brings about new physical effects and, for the few room-temperature examples, interesting prospects for applications in various fields. This interest is illustrated by the recent publication of several articles on multiferroics in high impact reviews over the last five years. The main...

A mechanism for the switching behavior of (111)-oriented Pb(Zr, Ti)O3-based 1 × 1.5 μm2 capacitors has been investigated using three-dimensional piezoresponse force microscopy (3D-PFM). A combination of vertical and lateral piezoresponse force microscopy (VPFM and LPFM) has been used to map the out-of-plane and the in-plane components of the polarization. The three-dimensional polarization dist...

Thin films of PbTiO3, a classical ferroelectric, have been grown under tensile strain on single-crystal substrates of DyScO3. The films, of only 5 nm thickness, grow fully coherent with the substrate, as evidenced by synchrotron x-ray diffraction. A mapping of the reciprocal space reveals intensity modulations (satellites) due to regularly spaced polar domains in which the polarization appears ...