in this paper, the reasons of damage water pumps parts of the air compressor cooling system were studied. to reach this goal, the works like preparing metallographic samples, evaluation of structure, investigation of mechanical properties, the alloy parts detection and chemical analysis of deposit and corrosion products collected from the parts were performed. according to studies and results o...

This article reports the effects of various artificial aging methods and lubrication modes (dry, mist, wet) on the recorded cutting forces and chip morphology in drilling Al-Si-Mg (A356) cast alloys. In the course of this work, the work part sampled were as-received alloy (T0), solution heat-treated alloy (SHT) and then aged alloys at 155°C, 180°C, and 220°C (T4, T6, T61, T7), respectively. The...

In this research the effect of volume and morphology of eutectic carbides on tribological behaviour of Ni-Hard 4 cast irons have been investigated. Therefore, as a result of the fact that the carbon content effects the carbides morphology of Ni-hard cast irons, the chemical compositions of five different specimens were kept constant with the exception of the carbon content, which was varied fro...

To obtain high-performance Al-Si-based cast alloys, refinement and modification of Si phases are required. An Al-12Si/ZnS powder inoculant was designed fabricated using a chemical bath deposition method. The efficiency the for modifying eutectic phase in as-cast Al-12Si alloy studied. Results show that can significantly refine Al-Si alloys. best effect is achieved with 17.5wt.% powder. Coarse l...

In this research the effect of volume and morphology of eutectic carbides on tribological behaviour of Ni-Hard 4 cast irons have been investigated. Therefore, as a result of the fact that the carbon content effects the carbides morphology of Ni-hard cast irons, the chemical compositions of five different specimens were kept constant with the exception of the carbon content, which was varied fro...

In this study, the effect of Ce additions on microstructure evolution of Mg-7Gd-3.5Y-0.3Zn (wt %) alloys during the casting, homogenization, aging and extrusion processing are investigated, and novel mechanical properties are also obtained. The results show that Ce addition promotes the formation of long period stacking ordered (LPSO) phases in the as-cast Mg-Gd-Y-Zn-Ce alloys. A high content o...

The effect of 5 different surface conditioning methods on bonding of metal brackets to cast dental alloys was examined. The surface conditioning methods were fine (30-microm) or rough (125-microm) diamond bur, sandblasting (50-microm or 110-microm aluminum oxide [Al2O3]), and silica coating (30-microm silica). Fifty disc-shaped specimens of 5 different alloys (gold-silver, palladium-silver, nic...

Ti-5Sn-xMo (x = 0, 1, 3, 5, 7.5, 10, 12.5, 15, 17.5, and 20 wt %) alloys were designed and prepared for application as implant materials with superior mechanical properties. The results demonstrated that the crystal structure and mechanical properties of Ti-5Sn-xMo alloys are highly affected by their Mo content. The as-cast microstructures of Ti-5Sn-xMo alloys transformed in the sequence of pha...

During casting of aluminum alloys, the partially solidified material is submitted to thermally induced strains that can lead to severe casting defects, such as hot tearing. In this work, carried out in the frame of the European project VIR[CAST], the rheological behavior of a partially solidified AA5182 aluminum alloy has been investigated in order to provide constitutive equations to predict h...

The formation of the icosahedral phase, BCC (Body centred cubic) phase and nanocrystals are seen in the as-cast alloy with nominal composition of Mg4Zn94Y2. FCC (face centred cubic) phase and modulated structures are formed in the alloys with higher Y content (10% and 25% Y respectively). These phases are analysed keeping in view their relation to the quasicrystals of the Mg-Zn-Y system.