iron oxide nanoparticles were synthesized by coprecipitation method using ammonia as precipitation agent. most researchers usually add ammonia into the iron salt solution but in this work the salt solution drop wise has been added to the ammonia and the new obtained results were compared with those of other researches. magnetic properties of nanoparticles were measured by vsm. the effect of rea...

Objective(s):Iron oxide nanoparticles have found prevalent applications in various fields including drug delivery, cell separation and as contrast agents. Super paramagnetic iron oxide (SPIO) nanoparticles allow researchers and clinicians to enhance the tissue contrast of an area of interest by increasing the relaxation rate of water. In this study, we evaluate the dependency of hydrodynamic si...

zinc oxide (zno) nanoparticles were synthesized by spray pyrolysis method using an aqueous solution of zinc acetate at various concentrations from 5 to 25 wt%. the decomposition of precursor solutions was carried out at 800, 1000 and 1200ºc under different atomizing pressures. the crystal structure and morphology of synthesized nanoparticles were characterized by x-ray diffraction (xrd) spectro...

Ultra-violet protection and self-cleaning action of nano zinc oxide (ZnO) and titanium di-oxide (TiO2) with acrylic binder has been assessed on the cotton fabric using pad-dry-cure method. Different precursors, such as zinc acetate and titanium tetrachloride have been used to synthesize nanoparticles. Zinc acetate is synthesized into nanoparticle by wet chemical technique and titanium tetrachlo...

In this paper, synthesis of the flower-like zinc oxide was performed using microwave assisted dicationic ionic liquid [mmp(im)2 ]Br2 . The polycrystalline flower-like zinc oxide nanostructure was obtained when a suitable mole ratio (ionic liquid /zinc acetate) and short duration microwave was used. X-ray diffraction (XRD), scanning electron microscopy (SEM), and photoluminescence (PL) spectra w...

In this study adsorption of Cr(VI) from aqueous solution by Fe3O4 nanoparticles was investigated. Desorption process and recovery of nanoparticles using different solutions were then carried out, and it was observed that NaOH (0.5M) can remove 90% of adsorbed chromium ions. Following the completion of adsorption/ desorption cycles, it was determined that nanoparticles have still had a high abil...

introduction: the aim of this study was to evaluate the cytotoxicity of a new nano zinc-oxide eugenol (nzoe) sealer in comparison with ah-26 and pulpdent root canal sealers. methods and materials: the l929 mouse fibroblast cells were cultivated and incubated for 24, 48 or 72 h with different dilutions (1/1, 1/2, 1/4, 1/8, 1/16 and 1/32) of culture media previously exposed to either of the test ...

the photocatalytic degradation of betamethasone sodium phosphate was investigated in aqueoussuspensions of zinc oxide nanoparticular with diameter size 20 nm under a variety of conditions.different parameters such as irradiation time, the amount catalyst (0.12-0.8 g lh), initialconcentration of drug (10-50 mgljand initial ph values (ranging from 3 to ii) were investigatedin the presence of vari...