In the present investigation, an attempt has been made to use “exponential model” in the prediction of fatigue life without integrating the fatigue crack growth rate curve (FCGR). The obtained results are compared with experimental crack growth data obtained for 2024-T351 aluminum alloy for four bending V-Charpy specimens under constant amplitude loading in stress ratio range from 0.1 to 0.3 an...

In this work, the effects of loading condition and corrosion solution on the corrosion fatigue behavior of smooth steel wire were discussed. The results of polarization curves and weight loss curves showed that the corrosion of steel wire in acid solution was more severe than that in neutral and alkaline solutions. With the extension of immersion time in acid solution, the cathodic reaction of ...

Crack growth analysis has remained one of the challenging problems in the fracture mechanics of structures. On the other hand, the fatigue crack growth is a common phenomenon in the components of structures like airplanes, navies and fluid storages where the fracture due to crack should be considered in the design of these structures. In this paper, the finite volume method (FVM) is extended fo...

ÐFatigue crack initiation and multiplication of the unnotched SCS-6 silicon carbide ®ber-reinforced titanium matrix composites with di€erent matrix and interfacial properties have been investigated experimentally and analytically. Ti±15V±3Al, Ti±6Al±4V, and Ti±22Al±23Nb were chosen as matrix materials. The initiation and propagation of each individual matrix crack as a function of fatigue cycle...

A B S T R A C T Pump shafts used for power generation are susceptible to fatigue cracking while often in near-continuous operation. Technology based on torsional vibration is under development for condition-based assessment of shaft health. The focus of this paper is on the relationship between a crack, which propagated due to bending loads, and the torsional stiffness of the shaft. An analytic...

Although bulk silicon is not known to exhibit susceptibility to cyclic fatigue, micron-scale structures made from silicon films are known to be vulnerable to degradation by fatigue in ambient air environments, a phenomenon that has been recently modeled in terms of a mechanism of sequential oxidation and stress-corrosion cracking of the native oxide layer. To date, most stress-life (S=N ) fatig...

Fatigue cracking is one of the most common failure modes of various load-bearing structures. Even though sensors of many different types have been developed for crack detection, very few can monitor crack growth with a high sensitivity. This paper presents an antenna sensor that is capable of monitoring the growth of fatigue cracks with a sub-millimeter resolution. According to microstrip patch...

Bulk-metallic glasses (BMGs) are now candidate materials for structural applications due to their exceptional strength and toughness. However, their fatigue resistance can be poor and inconsistent, severely limiting their potential as reliable structural materials. As fatigue limits are invariably governed by the local arrest of microscopically small cracks at microstructural features, the lack...

The mechanisms of fatigue-crack propagation in ceramics and intermetallics are examined through a comparison of cyclic crack-growth behavior in ductile and brittle materials. Crack growth is considered to be a mutual competition between intrinsic mechanisms of crack advance ahead of the crack tip, which promote crack growth, and extrinsic mechanisms of crack-tip shielding behind the tip, which ...

The present paper examines crack growth in a range of aerospace and automotive structural adhesive joints under cyclic-fatigue loadings. It is shown that cyclic-fatigue crack growth in such materials can be represented by a form of the Hartman–Schijve crackgrowth equation, which aims to give a unique and linear ‘master’ representation for the fatigue data points that have been experimentally ob...