Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...

The aim of this work is to determine the fatigue life of 316L stainless steel. The mechanisms of fatigue of 316L stainless steels were investigated and discussed. The fatigue tests were carried out at constant-amplitude cyclic loading with load ratio R=0.1. Scanning Electron Microscope (SEM) is then used to examine the fracture surface. The results show that the fatigue limit of 316L stainless ...

Environment safety measurements have resulted in use of peroxide as bleaching chemical in place of chlorine and chlorine dioxide. Concentration and composition of chemicals affects corrosion aspects, the suitability of existing plant metallurgy and materials of construction of bleach plants. Accordingly long term immersion and electrochemical corrosion tests were conducted on stainless steel 30...

INTRODUCTION Intravascular coronary stenting has been used in the treatment of coronary artery disease (CAD), with a major limitation of in-stent restenosis (ISR). The 316 stainless steel has been widely used for coronary stents. In this study, we developed a novel coating method to reduce ISR by simultaneously coating vascular endothelial growth factor (VEGF) and anti-CD34 antibody on 316L sta...

miniscrews reportedly have failure rates as high as 10-30%.1-4 Miniscrew loosening or tipping can result from any of the following factors: • Insufficient bone quantity or quality at the insertion site.5-7 • Use of a screw of inadequate diameter or length.3,8-10 • Inappropriate intraosseous design.10-12 • Root contact during insertion.13 • Manipulation by the patient’s fingers or tongue.8 • Poo...

The evaporation of inertial confinement fusion first wall materials from unattenuated pellet X-rays and from radiation emitted by a cavit.y buffer qas is examined. The low vapor pressure and low X-ray attenuation coefficient of carbon give it a lower erosion rate than stainless steel, despite the larger thermal conductivity of Type 316 stainless steel. For the argon buffer gas containing 0.2% N...

T'b is comilitmication emphasizes the nieed for conltin1uouts conitrol of pH when macerating acidic plant tissues for the l)url)ose of isolating tightly coupled mitochondria. A useful device for such control is described. Mitochonidria capable of oxidative but not pl)osphorylative activity have been isolated fromli apple fruits wlhenl either alkaline homogeniates (5) or l)oIyvinylpyrrolidone (P...

Chloride-induced corrosion of carbon steel reinforcement is the main cause of deterioration of reinforced concrete (RC) structures in marine environments. One of the ways to protect RC structures from corrosion is to use corrosion-resistant stainless steel reinforcing bars. However, stainless steel is between six and nine times more expensive than carbon steel. Thus, its use can only be justifi...

Layers of high silica zeolites, synthesized with an organic structure directing agent (OSDA) and grown onto porous support structures, frequently suffer from the thermal stress during the removal of OSDA via the calcination process. The different thermal expansion coefficients of the zeolite and the support material, especially when stainless steel is used as a support, causes enormous tension ...