In-situ synchrotron X-ray microtomography has been employed to investigate the three-dimensional (3D) closure behavior of short fatigue crack in Ti-6Al-4V alloy. At a spatial resolution level 1 µm, tomography datasets were taken at two fronts observe time evolution (sometimes called 4D imaging). Owing high level, complex 3D morphology consisting deflections, facet paths and branching/overlap ca...

This paper investigates the phenomenon of slant fracture observed in stable tearing tests of many ductile materials, where an initially flat crack, loaded under remote Mode I conditions, tends to grow into a slant crack and stay in the slant configuration until final fracture. In an effort to identify potential reasons why cracks prefer to grow in a slant manner, three-dimensional finite elemen...

Passivation hermiticity is always a concern in integration circuit fabrication and application. Passivation stress is one of the key factors for the passivation integrity. In this paper, passivation stress is investigated as a function of top metal profiles with a 3Dimentional Finite Element Modeling (3D FEM). A new structure is proposed for reducing the passivation stress at the corner of a to...

Concrete is the main constituent material in many structures. The behavior of concrete is nonlinear and complex. Increasing use of computer based methods for designing and simulation have also increased the urge for the exact solution of the problems. This leads to difficulties in simulation and modeling of concrete structures. A good approach is to use the general purpose finite element softwa...

initial cracks occur in high strength concrete sleepers for various reasons, such as shrinkage and wrong curing and long lifetime of over 50 years of sleepers. these cracks may lead to complete failure of the structure. in order to more accurately design the sleepers, fracture mechanics (not strength of materials) should be incorporated. in order to achieve this purpose, it is important to fore...

Detailed three-dimensional finite element analysis was carried out for area-array solder-bumped flip-chip packages. The analysis enabled determinations of accurate three-dimensional effects on stress distributions as well as local fracture behaviors under thermal load. The 3D analysis also estimated thermal fatigue life of solder bumps. Since dimensions of various components span more than thre...

Although, experimental studies have reported fracture at the corner of Steel Plate Shear Walls (SPSW), no study has been performed to investigate the crack effect, yet. Therefore, in this paper, the effect of crack at the corner of SPSWs on the seismic behavior of the system was investigated. Two probable cracks, that have been studies at the corner of SPSWs utilizing extended Finite Element me...

abstract rice can be cultivated in various soils but soil with heavy texture and low permeability is more appropriate for its growth than other types of soil texture. it’s assumed that existence of zeolite in soil can be effective for moisture retention and avoiding of occurrence of crack in soil. in order to investigation of the effect of zeolite on moisture status and hydraulic properties of ...

Abstract Steel fiber reinforced concrete (SFRC) will appear ununiform corrosion under chloride environment, resulting in corrosion-induced crack. However, the mechanism of crack corroded SFRC is not clear. In this paper, 3D mesoscale numerical model structure established, generation algorithm round straight steel provided, and are simulated by XFEM, at end damage characteristic studied. The res...

As fretting fatigue cracks are initiated at an early stage of life, the fretting fracture process is dominated by the stable growth of cracks. Hence the measurement of crack length is very important. This paper demonstrates the suitability of the DC potential drop technique for the measurement of fretting cracks. A calibration has been established for monitoring crack growth in BS L65 copper al...