Post-tensioning structures with metallic ducts risk corrosion, rupture or collapses due to chloride ingress. The use of tight corrugated polymer combined electrically isolated anchorages (EIT) changed the situation. Laboratory and many field applications proved tightness duct, showing resistance values higher much than 50 kΩm, acceptance criteria for a duct. most important fact is that EIT tend...

This paper studied the effects of reinforcement corrosion on bond performance between rebar and concrete. Tests were carried out to evaluate the degradation of bond between reinforcing steel and concrete for different corrosion levels of reinforcing steel. A series of 20 specimens of different concrete strength with various reinforcing steel corrosion levels were designed and manufactured. Each...

The filling of strand corrosion products during concrete crack propagation is investigated experimentally in the present paper. The effects of stirrups on the filling of corrosion products and concrete cracking are clarified. A prediction model of crack width is developed incorporating the filling proportion of corrosion products and the twisting shape of the strand. Experimental data on cracki...

The corrosion of Ag in an atmosphere of ozone and humidity with or without irradiation by ultraviolet (UV) light was investigated. A modified coulometric reduction technique was used, substituting sulphate solution for chloride solution, to prevent the spontaneous transformation of silver oxide corrosion product to chloride in the reduction solution. The presence of both ozone and UV radiation ...

ost assets depreciate, losing value over time as a result of wear and tear, age, or obsolescence. Corrosion, like depreciation, results in the often hidden cost of a non-cash expense — measurable in terms of reduced operating life — that reduces the value of assets. Many engineers in the chemical process industries (CPI) see corrosion on a “straight-line basis” in terms of repair, maintenance a...

Carbon dioxide corrosion has been widely studied in the field and laboratory. It is recognized that flow regime and metallurgy are important factors that influence in-situ corrosion rates but there are relatively few documented case studies that are able to separate the individual contributions of corrosion, flow regime and metallurgy on the observed corrosion damage. This paper deals with fail...

The roles of the alloying elements Mo, Cr, and W in resisting crevice corrosion of UNS N06022, UNS N06625, and UNS N10362 have been studied under galvanostatic conditions in 5 mol/L NaCl at 150°C. Corrosion damage patterns were investigated using surface analytical techniques such as scanning electron microscopy and optical imaging, and the corrosion products characterized by energy dispersive ...