A numerical technique for modeling fatigue crack propagation of multiple coplanar cracks is presented. The proposed method couples the extended finite element method (X-FEM) [Int. J. Numer. Meth. Engng. 48 (11) (2000) 1549] to the fast marching method (FMM) [Level Set Methods & Fast Marching Methods: Evolving Interfaces in Computational Geometry, Fluid Mechanics, Computer Vision, and Materials ...

An extensive experimental study of indentation and crack arrest statistics is presented for four different brittle materials (alumina, silicon carbide, silicon nitride, glass). Evidence is given that the crack length statistics is described by a universal (i.e., material independent) distribution. The latter directly derives from results obtained when modeling crack propagation as a depinning p...

In experiments where failure times are sparse, degradation analysis is useful for the analysis of failure time distributions in reliability studies. This research investigates the link between a practitioner’s selected degradation model and the resulting lifetime model. Simple additive and multiplicative models with single random effects are featured. Results show that seemingly innocuous assum...

THE PRINCIPLE of maximum energy dissipation rate is introduced as an energy criterion for crack dynamics. That allows us to explain observed limiting crack speeds in brittle materials, and to complete the crack dynamics formulation. The upper limits of the crack speed in perfectly elastic and elastic-plastic bodies are obtained. It is found that the theoretical maximum crack speed in an isotrop...

Quasi-static shear crack propagation in a linear elastic fluid-saturated porous solid c;Iuses a change of pore pressure on the crack plane if it is impermeable but not if it is permeable. Assuming that the pore pressure induced on the crack plane reduces the efTcclive compressive stress (total stress minus pore fluid pressure) and. as a result. the frictional resistance. we find that the energy...

Understanding how fractures develop in materials is crucial to many disciplines, e.g., aeronautical engineering, material sciences, and geophysics. Fast and accurate computer simulation of crack propagation in realistic 3D structures would be a valuable tool for engineers and scientists exploring the fracture process in materials. In the following, we will describe a next generation crack propa...

This paper deals with the effect of several residual stress profiles on the fatigue crack propagation in prestressing steel wires subjected to tension loading or bending moment. To this end, a computer program was developed to evaluate the crack front evolution on the basis of the Walker law. Results demonstrate that the absence of residual stresses makes the crack propagate towards a preferent...

Delamination is an important concern in the context of structural behaviour of laminated composite materials. It is known that delamination can diminish the stiffness and the strength of the material and promote structural failure. Delamination onset and growth is governed by interlaminar fracture toughness of the material. Delamination propagation is frequently dominated by mode II fracture; c...