Recent experimental and computational work by Link and associates has demonstrated that relatively small (W = 150 mm) single edge notched tension specimens (SE(T)) can be used to obtain crack arrest data high in the ductile-to-brittle transition of ferritic structural steel using dynamic computational techniques if a thermal gradient is utilized to aid in the crack arrest. Testing has been repo...

The growth of transverse cracks under expanding spherical contact in a model system consisted of soda-lime glass bonded to a polycarbonate substrate is observed in situ from below or from the polished edge of the bilayer. Abrasion or chemical etching is employed on the coating surfaces to control the initial fracture. In the limit case of monoliths, the crack mouth becomes fully engulfed by the...

The Mode I fracture toughness (KIC) of a small-grained Si3N4 was determined as a function of hot-pressing orientation, temperature, testing atmosphere, and crack length using the single-edge precracked beam method. The diameter of the Si3N4 grains was <0.4 μm, with aspect ratios of 2–8. KIC at 25°C was 6.6 ± 0.2 and 5.9 ± 0.1 MPa?m1/2 for the T–S and T–L orientations, respectively. This differe...

An elastic analysis is presented for the tensile stretching and bending of a plate containing a surface crack penetrating part-through the thickness, Fig. 1. The treatment is approximate, in that the two-dimensional generalized plane stress and KirchhoffPoisson plate bending theories are employed, with the part-through cracked section represented as a continuous line spring. The spring has both...

Enamel is the hardest tissue in the human body covering the crowns of teeth. Whereas the underlying dental material dentin is very well characterized in terms of mechanical and fracture properties, available data for enamel are quite limited and are apart from the most recent investigation mainly based on indentation studies. Within the current study, stable crack-growth experiments in bovine e...

Interface and interfacial cracks interacting with screw dislocations in piezoelectric bimaterials subjected to antiplane mechanical and in-plane electrical loadings are studied within the framework of linear piezoelectricity theory. Straight dislocations with the Burgers vector normal to the isotropic basal plane near the interface or interfacial crack are considered. The dislocations are chara...

The digital image correlation method is extended to the study of transient deformations such as the one associated with a rapid growth of cracks in materials. A newly introduced rotating mirror type, multichannel digital high-speed camera is used in the investigation. Details of calibrating the imaging system are first described, and the methodology to estimate and correct inherent misalignment...

Rotating machinery, such as steam turbo, compressor, and aeroengine etc., are widely used in many industrial fields. Among the important rotor faults, the fatigue crack fault, which can lead to catastrophic failure and cause injuries and severe damage to machinery if undetected in its early stages, is most difficult to detect efficiently with traditional methods. In the paper, based on the trut...

The evolution of surface damage in bilayers due to cyclic spherical indentation in the presence of incompressible lubricant is studied using an all-transparent glass/polycarbonate system as amodel formore practical applications such as dental crowns and rolling contact fatigue. In situ observations and post-mortem material sectioning reveal that inner cone cracks evolve sequentially from the co...

For crack growth along an interface between dissimilar materials the effect of combined modes I, II and III at the cracktip is investigated. First, in order to highlight situations where crack growth is affected by a mode III contribution, examples of material configurations are discussed where mode III has an effect. Subsequently, the focus is on crack growth along an interface between an elas...