Particleboard and solid wood stakes were treated with either an isocyanate or phenol formaldehyde resin and exposed in soil beds comprising three different soil types and two moisture contents. The treatments resulted in a marked improvement in the dimensional stability of particleboard but had no effect on solid wood. Higher moisture uptakes in stakes exposed in sandy soils indicated that the ...

In the earlier study about polymer network of phenolic and epoxies resins mixed with linseed oil, only Phencat 15 was used as the catalyst for the phenolic resin. In this study, Phencat 382 and UH (a urea hydrochloride solution based on a 1 : 1 mole ratio of urea : hydrochloric acid 32%) will be used as catalysts to study their effects on the polymer network of phenolic and epoxy resins mixed w...

Preparation of well-ordered continuous mesoporous carbon films without the use of an intermediate inorganic template was achieved by spin coating of a thermosetting phenolic resin, resorcinol/phloroglucinol/formaldehyde, and a thermally-decomposable organic template, Pluronic F127 (PEO106–PPO70–PEO106). The carbon films were deposited onto silicon, platinum/ silicon, copper, glass, and quartz s...

Fiberboard is a common interior material used both in China and the United States of America. The increase in demand for interior materials has raised concerns regarding combustibility of the materials. The pyrolysis characteristics of fiber, phenolic resin (PF), and nano kaolinclay (NK) were investigated using thermogravimetry. The fire performances of samples coated with a mixture of NK and P...

Six potentially important wood adhesives for gluing southern pine and white oak flakeboards were evaluated for their perfonnances in steam-injection pressing and conventional platen pressing. Of the six resins tested, polyisocyanate resin perfonned well in both steam injection and conventional platen pressings. Phenol-fonnaldehyde (PF) and melamine urea-fonnaldehyde (MUF) resins perfonned poorl...

Lignin modified phenol formaldehyde wood adhesives have been prepared by replacing phenol with the groundnut shell lignin (GNSL) at varying weight percentages. The optimization of weight percent incorporation of GNSL was carried out in respect to mechanical properties. It was found that a maximum of up to 50 wt.% of phenol in the phenol formaldehyde (PF) adhesive can be substituted by GNSL to o...

This study is to investigate the capability of producing lignin-based phenol-formaldehyde adhesive (LBPFA) with lignin derived from coir pith collected in Mekong Delta, Viet Nam. The LBPFA synthetic process underwent non chemical modifications minimize petrochemicals and energy. Effective factors as reaction time, temperature various contents phenol substitution were examined. Physical, thermal...

An experimental feasibility study of using ultrasound to accomplish the dificult desorption of phenol from activated carbon and polymeric resin adsorbents is discussed. The desorption rates of activated carbon were found to significantly increase by ultrasound at 40 kHz and 1.44 MHz. Attrition of the activated carbon due to cavitation could be prevented by operating at a higher frequency and wi...