This paper presents experimental results of wear process under dry and boundary lubricated metallic (AISI 1034/AISI 52100) contacting bodies with different surfaces morphologies subjected to a wide range of kinematic fretting conditions. Analysis of damage mode observed under such fretting conditions is elucidated in context of surfaces morphologies therefore associated with surface manufacturi...

A polycarbonate-based nanohybrid has been created containing 1 wt% of Bentone 2010, an organically modified montmorillonite. A micro-section on the nanohybrid obtained using focused ion beam (FIB) and field emission scanning electron microscopy (FESEM) was employed to observe the orientation of the nanoclay inside a polycarbonate (PC) matrix in the cross-section FIB-milled face. A micro-scratch...

The Ni-based coatings with different content of spherical tungsten carbide were deposited by plasma transfer arc welding (PTAW) method on 304 austenitic stainless steel sheets in this study. The microstructure and wear property of spherical tungsten carbide particle reinforced composite coatings were investigated by means of optical microscope, scanning electron microscope (SEM), X-ray diffract...

The present study examined wear characteristics of A356/melon shell ash particulate composites. Dry-sliding the stainless steel ball against specimen disc revealed the abrasive wear behavior of the composites under loads of 2 and 5N. The composite showed lower wear rate of 2.182 × 10-4 mm3/Nm at 20 wt% reinforced material under load of 5N. Results showed that wear rate decreased significantly w...

The effects of FC-4 cationic surfactant on electrodeposited Ag–PTFE composite coating using direct or pulsed currents were studied using scanning electron microscope (SEM), energy dispersive X-ray (EDS), optical microscope, and a linear tribometer. FC-4:PTFE in various ratios were added to a non-cyanide succinimide silver complex bath. Direct or pulsed current method was used at a constant curr...

Background: Improvement of the mechanical and tribological properties due to extrusion can be attributed to the improved density and excellent bond strength due to high compressive stress. Methods: To avoid the product defects mathematically contoured cosine profiled die was used for the thermomechanical treatment. Improvement of mechanical characterization like density, hardness, compression t...

The amorphous hydrogenated carbon coatings (a-C:H) deposited by plasmaassisted chemical vapour deposition (PACVD), and tetrahedral amorphous carbon coatings (ta-C) deposited by pulsed vacuum arc discharge were evaluated by scratch adhesion testing, load-carrying capacity testing and tribological testing in unlubricated and lubricated sliding conditions. The wear surfaces of the coatings and cou...