In this report, the environmental aspects of producing proton conducting ceramics are investigated by means of the environmental Life Cycle Assessment (LCA) method. The proton conducting ceramics BaZr0.8Y0.2O3-δ (BZY), BaCe0.9Y0.1O2.95 (BCY10), and Sr(Ce0.9Zr0.1)0.95Yb0.05O3-δ (SCZY) were prepared by the sol-gel process. Their material requirements and environmental emissions were inventoried, ...

Air concentrations of respirable crystalline silica were measured in eleven (11) high school ceramics classrooms located in Salt Lake County, UT, USA. Respirable dust was collected on PVC filters using precision flow pumps and cyclone samplers (n = 44). Filters were subsequently analyzed for respirable dust and percent crystalline silica content. The geometric mean of the silica concentrations ...

An efficient solid-state approach was established to synthesize (K0.5Na0.5) NbO3 ceramics using calcination kinetics and microwave assisted sintering. Milling of carbonate and oxide raw materials were carried out for 15h to obtain homogeneous nano particles. The crystallite size of 5.30 nm was obtained for the KNN system after calcination through optimized parameters and observed to be stoichio...

Ceramics used for the repair and reconstruction of diseased or damaged parts of the musculo-skeletal system, termed bioceramics, may be bioinert (alumina, zirconia), resorbable (tricalcium phosphate), bioactive (hydroxyapatite, bioactive glasses, and glass-ceramics), or porous for tissue ingrowth (hydroxyapatite-coated metals, alumina). Applications include replacements for hips, knees, teeth, ...

Based on precursor powders with a size of 200-300 nm prepared by the low-temperature solid reaction method, phase-pure YFeO₃ ceramics are fabricated using spark plasma sintering (SPS) at different temperatures. X-ray diffraction (XRD) and scanning electron microscopy (SEM) reveal that the high-purity YFeO₃ ceramics can be prepared using SPS, while the results from X-ray photoelectron spectrosco...

1. Introduction Using solid state thermolysis of pre-ceramic polymers, it is possible to produce amorphous Si-(B-)C-N ceramics which are a new form of a glassy-like state with an enormous stability range up to 1700 °C (see e. g. [1,2]). Si-(B-)C-N ceramics are promising candidates for the design of ultra-high temperature stable structure materials. The thermal stability and the crystallization ...

1 − x)Pb(Mg1/3Nb2/3)O3−xPbTiO3 (x = 0, 5, and 10 mol%) ceramics were prepared using a conventional mixed oxide solid state reaction method. The low-temperature relaxor behavior of (1 − x)Pb(Mg1/3Nb2/3)O3–xPbTiO3 ceramics were examined in the temperature range from 120 to 523 K. A broad dielectric maximum that shifted to higher temperatures with increasing frequency, signified the relaxor-type b...

Ceramics bonding is becoming an important technology and has found wide applications in different engineering and electronic industries. In this paper, furnace bonding of ceramics using solder glass frit was investigated with emphasis on the effects of surface treatment and bonding conditions on bonding strength. Alumina (Al2O3) sheet and SCHOTT solder glass G017-393 were used as the base and b...

The aim of this study was to clarify the effects of micro surface defects introduced by the focused ion beam (FIB) technique on the fracture strength of ceramics. Three-point bending tests on alumina-silicon carbide (Al₂O₃/SiC) ceramic composites containing crack-like surface defects introduced by FIB were carried out. A surface defect with area in the range 19 to 35 µm was introduced at the ce...

Transparent Ce:YAG ceramics were synthesized from the Ce:YAG powder which was produced by co-preparation method of the hydroxides. The Ce:YAG ceramics exhibit a broad emission band peaked at 530 nm due to the 5d→4f transition of Ce 3+ . The transmittances of the samples obtained were 70 ~ 87 % at 800 nm. The absorption coefficient and emission intensity of Ce 3+ were increased with the increase...