Superelastic wires and diamond-shaped stent surrogates were manufactured from Nitinol rods and tubing, respectively, from five different mill product suppliers - Standard VAR, Standard VIM, Standard VIM+VAR, Process-Optimized VIM+VAR, and High-Purity VAR. High-cycle fatigue tests up to 10(7) cycles were conducted under tension-tension conditions for wires and bending conditions for diamonds. Th...

Low cycle fatigue–creep is the main reason for the failures of many engineering components under high temperature and cyclic loading. Based on the exhaustion of the static toughness and dissipation of the plastic strain energy during fatigue failure, a new low cycle fatigue–creep life prediction model that is consistent with the fatigue–creep damage mechanism and sensitive to the fatigue damage...

introduction: this study investigated the fatigue and fracture modes of race and protaper rotary instruments. materials & methods: fatigue resistance was evaluated by rotating the files 30 ° or 60 ° and with 2 or 5mm radius of curvature. race taper 06 size 25 and protaper f1 files (n=40) were used. the number of rotations to failure was analyzed by two-way anova and independent sample     t-tes...