Delamination is an important concern in the context of structural behaviour of laminated composite materials. It is known that delamination can diminish the stiffness and the strength of the material and promote structural failure. Delamination onset and growth is governed by interlaminar fracture toughness of the material. Delamination propagation is frequently dominated by mode II fracture; c...

Fracture behavior of Cu-Ni laminate composites was investigated by tensile testing. It was found that as the individual layer thickness decreases from 100 to 20 nm, the resultant fracture angle of the Cu-Ni laminate changes from 72° to 50°. Cross-sectional observations reveal that the fracture of the Ni layers transforms from opening to shear mode while that of the Cu layers keeps shear mode. C...

Assessment of the correlation between rock brittleness and rock fracture toughness has been the subject of extensive research works in the recent years. Unfortunately, the brittleness measurement methods have not yet been standardized, and rock fracture toughness cannot be estimated satisfactorily by the proposed indices. In the present study, statistical analyses are performed on some data col...

The failure process ahead of a mode I crack advancing in a ductile thin metal plate or sheet produces plastic dissipation through a sequence of deformation steps that include necking well ahead of the crack tip and shear localization followed by a slant fracture in the necked region somewhat closer to the tip. The objective of this paper is to analyze this sequential process to characterize the...

OBJECTIVES The aim of the present investigation was to study the influence of a reduced bone support on the fracture resistance of endodontically treated teeth restored with glass fibre-reinforced posts (FRC). METHODS 30 caries-free maxillary central incisors were divided into 3 groups (n=10). Endodontic treatment was performed. Teeth were flattened 2 mm above the cemento-enamel junction. Gro...

modelling of crack propagation by finite element method under mixed mode conditions is of prime importance in fracture mechanics. this paper describes an application of finite element method to the analysis of mixed mode crack growth in linear elastic fracture mechanics. crack growth process is simulated by an incremental crack-extension analysis based on the maximum principal stress criterion,...

The digital image correlation technique is applied to investigate mixed-mode (I/II) fracture in five aerospace epoxy formulations, four of which are experimentally toughened. Stress intensity factors are extracted from displacement fields using the Williams method for a range of mode mixities. From these measurements, values of an effective resin KIIc are deduced and these are shown to have a s...

PURPOSE There is a continuing need to improve the prediction of hip fractures to identify those at highest risk, enabling cost-effective use of preventative therapies. METHODS The aim of this work was to validate an innovative imaging biomarker for hip fracture by modelling the shape and texture of the proximal femur assessed from dual energy X-ray absorptiometry (DXA) scans. Scans used were ...

The fracture and crack growth of mechanical structures is a usual phenomenon which is due to the application of tensile, cyclic loading or thermal stresses on the structure. So introducing of methods to prevent the crack growth is useful. Afterward, one of the repairing methods of crack growth, consisting to make a hole in the crack tip to elimi-nate the sharp corners, was explained. This metho...

Abstract The paper contains the results of an experimental investigation fatigue crack development under mixed-mode I + II and III in heat-treated 42CrMo4 steel. Tests were performed on compact tension shear specimens rectangular cross-section for III. Mixed-mode tests conducted 30 60° loading angle, while test was 45°. Additionally, presents fracture analysis path development.