Both magnetic-field-induced reverse martensitic transformation (MFIRMT) and mechanical properties are crucial for application of Ni-Mn-Sn magnetic shape memory alloys. Here, we demonstrate that substitution of Fe for Ni can simultaneously enhance the MFIRMT and mechanical properties of Ni-Mn-Sn, which are advantageous for its applications. The austenite in Ni44Fe6Mn39Sn11 shows the typical ferr...

The austenite-to-martensite transformation in a partially hardened stainless steel containing 17wt %Cr, 7wt %Ni and 1wt % Al was investigated with Vibrating Sample Magnetometry and Electron Back-Scatter Diffraction. Magnetometry demonstrated that measurable martensite formation can be suppressed on fast cooling to 77K as well as on subsequent fast heating to 373 K. Surprisingly, martensite form...

A new experimental approach is used to quantify the full field heterogeneous strain accommodation associated with martensitic phase transformation in Nickel–Titanium at the microstructural length scale. Local deformation measures were matched with underlying microstructural characteristics obtained by EBSD, providing point-by-point correlation between transformation extent and microstructure. I...

Single crystals of Co48Ni22Ga30 have been synthesized using a modified Bridgman method. The ability to solidify and retain single phase B2 austenite was found to depend not only on the starting composition and growth rate, but also the ability to maintain sufficiently high cooling rates to avoid the precipitation of a Co-rich FCC phase during post-solidification cooling. DSC measurements on the...

It can be challenging to properly identify the phases in electro-polished duplex stainless steel using optical microscopy or other characterization techniques. This letter describes magnetic force microscopy to properly identify the phases in electropolished duplex stainless steel. The results are also confirmed PM anoindentation with the current sensing atomic force and scanning Kelvin probe f...

Phase transformation temperature is one of the most important parameters for the shape memory alloys (SMAs). The most popular method to determine these phase transformation temperatures is the Differential Scanning Calorimeter (DSC), but due to the limitation of the DSC testing itself, it made it difficult for the finished product which is not in the powder form. A novel method which uses the U...

A PM approach is investigated in the context of extremely fine low temperature bainitic steels with a reasonable combination of ultimate tensile strength and uniform elongation. The strategy consists of three steps. First, ball milling is used for mechanical alloying and to create a large density of interfaces prior to sintering. In the second step, spark plasma sintering is used as a rapid con...

Strong steels also have to be tough and hence rely on fine microstructures such as bainite or martensite, produced commercially by continuous cooling transformation. Depending on the detailed requirements, the steel-design process may explicitly require other higher temperature phases to be absent in the final microstructure. Such a procedure can be made easier by the availability of a good met...

The nucleation and growth mechanisms of Ni5A13 precipitates and microtwinned plates in B2 austenite and 2M (3R) martensite phases are described on the basis of conventional and high resolution electron microscopy. In the Ni62.5A137.5 B2 austenite matrix short annealings at 550°C introduce three-pointed star shaped precipitates consisting of twin related parts of different variants of the Ni5A13...

The nucleation of bcc austenite in a single crystal of a mechanically stabilized 2H-martensite of Cu-Al-Ni shape-memory alloy is studied. The nucleation process is induced by localized heating and observed by optical microscopy. It is observed that nucleation occurs after a time delay and that the nucleation points are always located at one of the corners of the sample (a rectangular bar in the...