A model is presented for the dynamic finite element analysis of ceramic microstructures subjected to multi-axial dynamic loading. This model solves an initial-boundary value problem using a multi-body contact scheme integrated with interface elements to simulate microcracking at grain boundaries and subsequent large sliding, opening and closing of interfaces. A systematic and parametric study o...

The effect of stitching on mode I and mode II strain energy release rates for debond configurations is studied using an analysis based on plate finite elements and the virtual crack closure technique. The stitches were modeled as discrete nonlinear fastener elements with a compliance determined by experiment. The axial and shear behavior of the stitches was considered with both the compliances ...

Abstract: The high cycle fatigue property of carburized 20Cr gear steel was experimentally investigated under axial loading with a stress ratio of zero. The test results show that this steel exhibits gradually decreasing S-N characteristics, and the fatigue strength corresponding to 109 cycles is about 455 MPa. Based on the observation of fracture surfaces, the interior inclusion fisheye-induce...

Initial cracks occur in high strength concrete sleepers for various reasons, such as shrinkage and wrong curing and long lifetime of over 50 years of sleepers. These cracks may lead to complete failure of the structure. In order to more accurately design the sleepers, fracture mechanics (not strength of materials) should be incorporated. In order to achieve this purpose, it is important to fore...

Compositionally graded glass-filled epoxy sheets with edge cracks initially along the gradient are studied under dynamic loading conditions. Specimens with monotonically varying volume fraction of reinforcement are subjected to mixed-mode loading by eccentric impact relative to the crack plane. The optical method of Coherent Gradient Sensing and high-speed photography are used to map transient ...

Crack-growth experiments in human dentin have been performed in situ in an environmental scanning electron microscope to measure, for the first time, the crack-growth resistance curve (R-curve) for clinically relevant (<250 microm) crack extensions and to simultaneously identify the salient toughening mechanisms. "Young" dentin from donors 19-30 years in age and "aged" dentin from donors 40-70 ...

Shielding interaction effects of two parallel edge cracks in finite thickness plates subjected to remote tension load is analyzed using a developed finite element analysis program. In the present study, the crack interaction limit is evaluated based on the fitness of service (FFS) code, and focus is given to the weak crack interaction region as the crack interval exceeds the length of cracks (b...

It is considered that the process of fatigue fracture could be arranged the three classes, i.e., crack initiation, crack propagation and fracture. Of these the second process is important from the following point of view. (1) As has so far been reported in many publications, the importance of crack propagation process in total fatigue life increases in proportion to the increase in the stress c...

In this work we describe a series of impact experiments performed on PMMA/4340 steel edge cracked bimaterial plates. Specimens were impacted at 20 m SK’ in a one point bend configuration using a high speed gas gun. Dynamic interfacial crack propagation was observed using the optical method of Coherent Gradient Sensing and high speed photography. Very high crack tip accelerations (IO’ m SF’) and...

In this study, an analytical model is developed to study crack breathing behavior under the effect of crack location and unbalance force. Crack breathing behavior is determined using effectual bending angle by studying the transient change in closed area of the crack. The status of the crack of a balanced shaft is symmetrical about shaft rotational angle and the duration of each crack status re...