During the steelmaking process, a great amount of slag is generated as by-product. Vanadium-bearing slags are classified hazardous and require special handling storage due to toxicity vanadium pentoxides. At same time, such valuable sources for recovery vanadium. The present work reviews investigations on from CaO-SiO2-FeO-V2O5 thin film under neutral oxidizing conditions in temperature range 1...

The influence of Al2O3 in the range 10–20 mass% and TiO2 0.55–5 on flow behavior, viscosity, density, surface tension molten industrial blast furnace slag with CaO/SiO2 = 1.13 is investigated using a high-temperature microscope, rotating viscometer, maximum bubble pressure method. measurement results show that acts as network former studied CaO–SiO2–MgO–Al2O3–TiO2 slags. With an increase conten...

The titanium industry can hardly bypass the titania-containing slags, and slag physicochemical properties are essential in metallurgical reactor design process control. TiO2–FeO-based slags TiO2–SiO2–CaO-based main systems resource utilization processes. To elaborate role of TiO2 including redox ratio, liquidus temperature, viscosity, electrical conductivity, density, surface tension, thermal s...

The phosphorus partition between the unkilled liquid crude steel and high basicity (CaO/SiO2 = 4.2), basic oxygen furnace (BOF) slags with varying compositions of Al2O3, TiO2, MnO is studied at temperatures 1600 1650 °C. tests are conducted in both “slag-to-metal” “metal-to-slag” directions for durations 30 60 min. measured results compared values reported literature found to be good agreement ...