The paper deals with the corrosion behavior of stainless steels as candidate materials for biofuel production plants by liquefaction process of the sorted organic fraction of municipal solid waste. Corrosion tests were carried out on AISI 316L and AISI 304L stainless steels at 250 °C in a batch reactor during conversion of raw material to bio-oil (biofuel precursor), by exposing specimens eithe...

Environmentally friendly and cyanide-free sulfate bath under continuous current and the corrosion behavior of electrodeposits of zinc-iron alloys were studied by means of electrochemical tests in a solution of 3.5% NaCl in presence and absence of glycine. The effects of pH on the quality of Zn-Fe coatings were investigated in order to improve uniformity and corrosion protection performance of t...

In this study, a plasma electrolytic oxidation (PEO) process was used to form titanium-aluminum oxide coating on aluminized steel. The present work was mainly to study the effects of treatment time of PEO process on properties of the titanium coating. A potentiodynamic polarization corrosion test was employed to investigate the corrosion resistance of the coating. The friction coefficient and w...

The present study shows a novel method for the synthesis of uniformly-shaped poly(othophenylediamine) (PoPD) nanofibers by chemical oxidative polymerization method for application towards smart corrosion resistance coatings. Transmission Electron Microscopy (TEM) and Scanning Electron Microscopy (SEM) studies confirm morphology of PoPD with three dimensional (3D) networked dendritic superstruct...

There is a wide variety of dental alloys, ranging from nearly pure gold and conventional gold-based alloys to alloys based on silver, palladium, nickel, cobalt, iron, titanium, tin, and other metals (Table 1). The types of dental alloys have increased significantly since 1980s in order to change the market price of gold and palladium. Although gold alloys are the mate‐ rials of choice in this a...

Corrosion of concrete reinforcing steel in highway structures has traditionally been related to chloride ions. However, another cause of reinforcing steel corrosion is concrete carbonation which decreases the pH of the pore solution, Carbonation-induced corrosion tends to develop later and proceeds at slower rates than chloride-induced corrosion. Since very long service life goals are currently...

Corrosion of steel reinforcement is one of the main durability problems facing reinforced concrete infrastructures worldwide. This paper will summarize the results of a multi-phase experimental program undertaken at the University of Waterloo to investigate the viability of using externally bonded fiber reinforced polymer (FRP) laminates to rehabilitate corrosion-damaged reinforced concrete bea...

The life of a concrete bridge exposed to deicing salt or seawater has often been limited by corrosion of the steel reinforcement. The service life of a concrete structure, degraded by corrosion, is considered to be the sum of the initiation and propagation periods. The initiation phase is the time required for sufficient accumulation of aggressive species at the rebar surface to initiate corros...

Experimental investigation was conducted on corroded composite push-out specimens to study the behavior of shear studs subjected to fatigue loading. A total of eight standard EC4 push-out specimens were tested. The expected corrosion rate of test specimens ranged from 0 to 50%. The main purpose of these tests was to determine the fatigue life and the reduction effect caused by the corrosion on ...

The electrochemical behavior and the corrosion rate of aluminum electrode have been evaluated in different pH solutions in absence and presence of aggressive anion, using open-circuit potential measurements and potentiodynamic polarization technique. Also, the corrosion inhibiting effects of ortho, meta and para toludine in a solution of pH4 containing 0.1M sodium chloride was investigated usin...