BACKGROUND Pulpal reaction to restorative materials depends on marginal microleakage, which is a dynamic phenomenon that allows bacteria and fluids to traverse across the tooth-restoration interface. Glass-ionomer cement (GIC) exhibits low microleakage due to direct bonding to tooth structures. Hydroxyapatite (HAP) based on the similarity with tooth structure may decrease the microleakage. The ...

BACKGROUND Moisture sensitivity and dissolution has been a known drawback of glass ionomer cement (GIC). When used as a luting agent for cementation of casted indirect restoration, the exposed cement at the margins is often a primary factor for marginal leakage and consequent failure of the restoration. The following in vitro study was planned to evaluate the effect of a marginal sealant on GIC...

OBJECTIVE This in vitro study evaluated the influence of luting agents on ultrasonic vibration time for intraradicular cast post removal. MATERIAL AND METHODS After endodontic treatment, 30 roots of extracted human canines were embedded in resin cylinders. The post-holes were prepared at 10 mm depth and their impressions were taken using autopolymerizing acrylic resin. After casting procedure...

background and aims: new dentin bonding agents and techniques have been developed to reduce microleakage and create higher bond strength. this in-vitro study compared the microleakage of three resin-based adhesives versus a gic-based adhesive on class v composite restorations.  materials and methods: class v cavities were prepared on the buccal surfaces of 72 sound premolars, randomly assigned ...

The aim of this investigation was to compare the clinical performance of a glass ionomer cement (GIC) with a composite resin when used for direct bonding of standard edgewise orthodontic brackets. Fourteen patients (10 females, four males), in whom 242 teeth were bonded with brackets, were divided into two groups: GIC (121 teeth) and composite (121 teeth). The brackets were allocated to alterna...

OBJECTIVE The aim of this study was to assess the frequency of cement residues after cementation of CAD/CAM monolithic zirconia crowns on customized CAD/CAM titanium abutments. MATERIALS AND METHODS Sixty premolars and molars were restored on Astra Tech Osseospeed TX™ implants using single monolithic zirconia crowns fixed on two types of custom-made abutments: Atlantis™ titanium or Atlantis™ ...

AIM The aim of this study was to evaluate the three-body wear-resistance of one type of restorative glass-ionomer cement (GIC). MATERIALS AND METHODS Specimen including conventional GIC (Ionofil Molar AC Quick: IMACQ), hybrid ionomer (Fuji II LC), and composite resin (Heliomolar) were tested in a wearing machine. In this machine, a 6 kg load was applied via pressable chromium-cobalt bar at 5,...

Context. An in vitro study carried out to evaluate and compare the effect of Cola drink on surface roughness of esthetic restorative materials. Purpose. To compare the effect of different immersion regimes in a Cola drink on surface roughness of esthetic restorative materials. Method. Two hundred samples were grouped into 4 equal groups of 50 samples each: Group I: conventional glass ionomer, G...

BACKGROUND Glass-ionomer cements perform a protective effect on the dentin-pulp complex considering the F ions release and chemical bonding to the dental structures. On the other hand, those materials have poor physic-mechanical properties in comparison with the restorative resin composite. The main aim of this work was to evaluate the influence of zirconia and/or alumina fillers on the microst...

Objective The aim of this study was to evaluate the retention of glass ionomer sealant, Vitro Molar® (DFL) and Ketac Molar Easy Mix® (3 m ESPE) as pit and fissure sealants on first permanent molars, fully or partially erupted. Methods The study sample consisted of 412 molars, among 110 children. The sealant retention was evaluated after 6 months of the application. Results The results were coll...