The effects of increasing nickel from 3 to 7 and 9 wt. % were investigated in high strength steel weld metals with 2 wt. % manganese. It was found that nickel additions were positive for strength but negative for impact toughness. Significant segregation of nickel and manganese to interdendritic regions was observed with the two higher nickel contents. In these weld metals a mainly martensitic ...

The effects of increasing the nickel content from 3 to 7 or 9 wt-% were investigated in high strength steel weld metals with 2 wt-% manganese. Nickel additions were beneficial to strength but detrimental to impact toughness. Significant segregation of nickel and manganese to interdendritic regions was observed at the two higher nickel contents. In these weld metals a mainly martensitic microstr...

The influence of the martensitic, martensitic+austenitic and austenitic structures in bending training on two-way shape memory effect (TWSME) in Ni-50.8 at %Ti and Ni-49.9 at %Ti alloys was studied. In addition of the primary structure, the effect of pre-strain, plastic strain, training cycle and training temperature on the TWSME was investigated. The prepared samples were trained in martensiti...

Neural network predictions suggested that strength of a high strength steel weld metal with 7 wt. % nickel and 0.5 wt. % manganese could be increased significantly at moderate expense to impact toughness by additions of carbon. Based on this, three experimental weld metals were produced with carbon levels between 0.03 and 0.11 wt. %. Mechanical test results were in agreement with predictions. W...

A fatigue test method by a miniaturized hourglass-shaped fatigue specimen has been developed for International Fusion Materials Irradiation Facility (IFMIF) and sufficient potential as the alternative to a conventional large specimen was presented. Furthermore, focused ion beam micro-sampling method was successfully applied to microstructural analysis on fracture process. Where, the effects of ...

Reduced activation ferritic-martensitic steel F82H was irradiated with 5 keV helium ions to introduce the surface damage. After the irradiation, the irradiated F82H was continuously exposed to 1.7 keV deuterium ions. The effects of the damages introduced by the helium ion irradiation on deuterium retention and desorption behavior of F82H were investigated. The HD desorption had a peak at around...

In the present study, the effect of grain size on the austenite stability was studied by nanoindentation tests in a 304L stainless steel. Thermomechanical processing based on cold rolling and annealing was used to produce two different types of austenite: ultrafine grained (UFG) austenite with the average grain size of 0.65 μm and coarse grained (CG) austenite with the average grain size of 12 ...

Neural network predictions suggested that the strength of a high strength steel weldmetal with 7 wt-% nickel and 0.5 wt-% manganese could be increased significantly at moderate expense to impact toughness by additions of carbon. Based on this, three experimental weldmetals were produced with carbon contents between 0.03 and 0.11 wt-%. Mechanical test results were in agreement with predictions. ...

Atom-probe tomography (APT) provides atomic-scale spatial and compositional resolution that is ideally suited for the analysis of grain boundaries. The small sample volume analyzed in APT presents, however, a challenge for capturing mesoscale features, such as grain boundaries. A new site-specific method utilizing transmission electron microscopy (TEM) for the precise selection and isolation of...