The curing behavior of lignin-based phenol-formaldehyde (LPF) resin with different contents of nano-crystalline cellulose (NCC) was studied by differential scanning calorimetry (DSC) at different heating rates (5, 10 and 20 ̊C/min) and the bonding property was evaluated by the wet shear strength and wood failure of two-ply plywood panels after soaking in water (48 hours at room temperature and f...

With the rapid growth in the ethanol fuel industry in recent years, considerable research is being devoted to optimizing the use of processing coproducts, such as distillers dried grains with solubles (DDGS), in livestock diets. Because these residues contain high fiber levels, they may be amendable to incorporation into biobased composites. Thus, the goal of this study was to demonstrate the v...

Plywood manufactured from thin veneer sheets of different species is one of the most traditional structural composite panels. The objective of this study was to produce experimental plywood panels using a temperature of 100 °C, which is 10 to 30% lower than typical press temperature of plywood manufacture. It was determined that shear strength characteristics of the samples were not adversely i...

A limited initial study was made to evaluate liquefaction of creosote-treated southern pine wood sawdust with liquefaction of birch wood powder as a control. The objective was to assess the feasibility of using creo_.._. sot&treated southern pine wood as a raw material for the-formulation-of-phenol-basedresmadhesives-Them liquefaction was conducted in the presence of phenol with sulfuric acid a...