A cyclic wet/dry accelerated corrosion test was used to compare the corrosion behavior of medium-Mn steel and Q345 steel. In terms of scanning electron microscope (SEM), using X-ray diffraction (XRD), electron probe microanalysis (EPMA), X-ray photoelectron spectroscopy (XPS), and analysis of the corrosion process, the results showed that the medium-Mn steel did not exhibit higher corrosion res...

Durability of reinforced concrete with respect to corrosion of reinforcement is one of the major aspects to be considered in the management of civil infrastructure systems. An accelerated laboratory test method developed at SERC where the concrete specimen containing rebar is subjected to polarization under a constant voltage in a sodium chloride solution. It is found that the current response ...

The behavior of corroded steel–concrete composite beams under hogging moment was studied by experimental investigation and theoretical analysis. A total of eight specimens, six of which had corroded shear studs, were tested. The corrosion rate of studs ranged from 0 to approximately 50%. The constant-current accelerated corrosion method was adopted to accelerate the corrosion process. The loadi...

In the present paper the corrosion properties of structured sheet metals were investigated. The aim of this work is to determinate the influence of the structuring process on the corrosion resistance of sheet metals. For this purpose, these sheets were examined by accelerated tests in corrosion chamber. The investigation was carried out using salt spray test. The experiment was conducted for th...

To improve the corrosion protection provided to prestressing strands, anti-bleed grouts are used to fill voids in post-tensioning ducts that result from bleeding and shrinkage of older portland cement grouts. Environmental differences caused by exposing the strands to dissimilar grouts, however, have the potential to cause rapid corrosion. Portland cement grout, gypsum grout, and four commercia...

Hydrostatic pressure effects on pitting initiation and propagation in X70 steel are investigated by evaluating metastable pitting probability using electrochemical methods and immersion corrosion tests in containing chlorine ion solution. Potentiodynamic tests indicated that hydrostatic pressure can decrease the breakdown potential and lead to a reduced transpassivity region. Metastable test re...

This paper presents an experimental investigation on the crack width induced by the corrosion of reinforcing steel bars in concrete. Reinforcing steel bars with different diameters were corroded using an accelerated test in three types of concrete members, including 24 beams with corroded stirrup and 20 beams with corroded longitudinal reinforcing steel bars. The corrosion patterns and rusts ch...

The corrosion behavior of pure Ti under a solid NaCl deposit in a wet O2 flow at 600 ̋C has been studied. The results showed that the corrosion rate was greatly accelerated by solid NaCl, which destroyed the compact and protective TiO2 scale to yield non-protective N4Ti5O12 and other products. Detailed scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDX), and...

In corrosion protection study, it is important to develop economically attractive test method for mitigation of corrosion damage of coated structure. Faster predication of protective behavior of any coating is a big challenge for the coating industries. In present work, in-house waterborne anticorrosive coating system was selected for study. The corrosion protection of coating evaluated as per ...