In this work, a simple and effective way to modify the support surface is developed and a nanostructure ceramic support to facilitate deposition of a defect-free overlying micro and meso (nano) porous membrane is obtained. To achieve high performance nanocomposite membranes, average pore size of outer surface of support was reduced by dip-coating in submicron and nano α-alumina slurries. In...

Simple nanoporous alumina matrix modification procedure, in which the electrically highly insulating alumina barrier layer at the bottom of the pores is replaced with the conductive layer of the gold beds, was described. This modification makes possible the direct electron exchange between the underlying aluminum support and the redox species encapsulated in the alumina pores, thus, providing t...

In an Al2O3-TiO2 mixed oxide system, the incorporation of TiO2 to alumina is known to increase the acidity of the resulting mixed oxide; depending strongly on the preparation method and the titania concentration. When using TiO2 as a support of NiMo catalysts, initial catalytic activity in hydrodesulfurization reactions is much higher than that on catalysts based on pure alumina. One of the mai...

A particular type of mesopore extrudates gamma alumina was prepared; which is used as the catalyst in the heavy oil desulfurization unit. Extrudates gamma-alumina support has been made of the boehmite powder from Nephlinsinite mine ores (Surface Area (S.A.) >200 m2/g, Pore Volume (P.V.) =0.48 cm3/g, Average Pore Diameter (A.P.D.) = 8.10 nm); then, many samples of extru...

The interaction of rhenium oxide with an alumina support is examined over a wide range of conditions (rhenium oxide loading, calcination temperature and environment) using laser Raman spectroscopy (LRS) and X-ray absorption near-edge spectroscopy (XANES). These structural probes reveal that supported rhenium oxide on alumina is present as an atomically dispersed surface [ Re04] ads species coor...

Simple nanoporous alumina matrix modification procedure, in which the electrically highly insulating alumina barrier layer at the bottom of the pores is replaced with the conductive layer of the gold beds, was described. This modification makes possible the direct electron exchange between the underlying aluminum support and the redox species encapsulated in the alumina pores, thus, providing t...

A zeolite NaA (A-type zeolite of ca. 0.4 nm pore size; Linde Type A, LTA) membrane for the dehydration of alcohol was characterized by X-ray diffraction analysis (XRD). Also, the relationship between the X-ray absorption and the EtOH/H2O pervaporation (PV) dehydration performance (water selectivity and permeation flux) of the LTA membrane was first investigated. The LTA membranes used here were...

Mesoporous Ni–alumina catalysts (Ni–alumina-pre and Ni–alumina-post) were synthesized by one-step sol–gel method using micelle complex comprising lauric acid and nickel ion as a template with metal source and using aluminum sec-butoxide as an aluminum source. The Ni–alumina catalysts showed relatively high surface areas (303 m/g for Ni–alumina-pre and 331 m/g for Ni–alumina-post) and narrow por...

A crackand pinhole-free composite membrane consisting of an a-alumina support and a modified y-alumina top layer which is thermally stable up to 1100°C was prepared by the sol-gel method. The supported thermally stable top layer was made by dipcoating the support with a boehmite sol doped with lanthanum nitrate. The temperature effects on the microstructure of the (supported and unsupported) La...

Carbon nanotubes (CNTs) were incorporated into alumina/polyethersulfone hollow fibre membranes to enhance the mechanical property and the efficiency of water treatment. Results show that the incorporation of CNTs can greatly limit the formation of large surface pores, decrease the void size in support layers and improve the porosity and pore connectivity of alumina/polyethersulfone membranes. A...