The macroparticle content of titanium films deposited using a steered vacuum cathodic arc has been investigated. It has been found that the macroparticle number decreases with increasing steering magnetic field strength, and experimental results are found to be consistent with the model in which the number and mass of macroparticles arising from a cathode spot are proportional to the cathode sp...

TiN films were prepared by the Cathodic arc evaporation deposition method under different negative substrate bias. AFM image analyses show that the growth mode of biased coatings changes from 3D island to lateral when the negative bias potential is increased. Nanohardness of the thin films was measured by nanoindentation, and residual stress was determined using Grazing incidence X ray diffract...

Hard coatings such as titanium nitride (TiN) and chromium nitride (CrN) are widely used in cutting and forming tools against wear and corrosion. In the present study, hard coating films were deposited onto AISI 1070 steels by a cathodic arc evaporation plating (CAVP) technique. These samples were subjected to wear in a conventional lathe for investigating the tribological behaviour of coating s...

Hard coatings can extend the life time of a tool substantially and enable higher cutting speeds which increase the productivity in the cutting application. The aim with this thesis is to extend the understanding on how the microstructure and mechanical properties are affected by high temperatures similar to what a cutting tool can reach during operation. Thin films of ZrAlN and TiAlN have been ...

in the present study, the effects of growth defects and chromium content loss on the degradation of corrosion andpassivation of cathodic arc evaporation (cae-pvd) of stainless steel coating were investigated in 2 m sulphuricacid solution. eds analysis indicated that the micro-particles were obtained during the coating growth. in addition,it was detected that the growth defects had poor adhesion...

In the present study, CrN, TiN and (Ti, Cr)N coatings were deposited on D6 tool steel substrates. Physical and mechanical properties of coatings such as microstructure, thickness, phase composition, and hardness were evaluated. Phase compositions were studies by X-ray diffraction method. Mechanical properties were determined by nano-indentation technique. The friction and wear behaviour of the ...

In this investigation PVD Ti-Cr)N coatings were deposited on hardened and tempered tool steel substrates using reactive arc evaporation. Physical and mechanical properties of coatings such as roughness, thickness, phase composition, hardness and modulus young and coefficient friction were evaluated. Phase compositions were studies by X-ray diffraction method. The surface microstructure and morp...