Using molecular dynamics with an accurate many-body potential for metallic Tantalum, we studied crack propagation in a pre-notched nano-slab under uniaxial strain in a [100] direction. We study dislocation emission from the crack tip for various strain rate and temperatures, focusing on the influence of the local temperature at the crack tip on the propagation of the crack. We find a close conn...

fast fracture is one of the major failure modes in brittle polymers. generally, crack growth in these polymers may occur under combined tensile-shear loading. however, the fracture test data reported previously for some dental restorative resins can not be predicted by using the available fracture criteria.in this paper, a modified fracture criterion is used for estimating the fracture load for...

Coherent twin boundaries (CTBs) in nano-twinned materials could improve crack resistance. However, the role of the CTBs during crack penetration has never been explored at atomic scale. Our in situ observation on nano-twinned Ag under a high resolution transmission electron microscope (HRTEM) reveals the dynamic processes of a crack penetration across the CTBs, which involve alternated crack ti...

The Eshelby tensor E has vanishing divergence in a homogeneous elastic material, whereas the invariance of the crack tip J integral suggests, in accord with known solutions, that the product rE will have a finite limit at the tip. Here r is distance from the tip. These considerations are shown to lead to two general integrals of the equations governing singular crack tip deformation fields. Som...

The role of crack-tip shielding in in ̄uencing mixed-mode (mode I‡ II) fatigue-crack growth thresholds for large, through-thickness cracks in a Ti±6Al±4V turbine blade alloy is examined under high-cycle fatigue loading conditions, i.e., at a loading frequency of 1000 Hz in ambient temperature air for load ratios (Kmin=Kmax) of R ˆ 0:1±0.8. Techniques are developed to quantify crack-tip shielding...

An assessment of the plasticity-induced crack-closure concept is made, in light of some of the questions that have been raised on the validity of the concept, and the assumptions that have been made concerning crack-tip damage below the crack-opening stress. The impact of using other crack-tip parameters, such as the cyclic crack-tip displacement, to model crack-growth rate behavior was studied...

In order to monitor the crack tip propagation of aluminum alloy, this study investigates the variation of the spectrum characteristics of a fiber Bragg grating (FBG), combined with an analysis of the spectrum simulation. The results identify the location of the subordinate peak as significantly associated with the strain distribution along the grating, corresponding to the different plastic zon...

MATCHED asymptotic expansions are used to examine the stress and pore pressure fields near the tip of a plane strain shear (mode II) crack propagating on an impermeable plane in a linear elastic diffusive solid. For propagation speeds V that are large compared with c/I, where c is the diffusivity and I is the cracklength, boundary layers are required at the crack-tip and on the line ahead of th...

Despite decades of study, the atomic-scale mechanisms of fatigue crack growth remain elusive. Here we use the coupled atomistic–discrete dislocation method, a multiscale simulation method, to examine the influence of dislocation glide resistance on near-threshold fatigue crack growth in an aluminum alloy. The simulations indicate that the threshold increases with an increase in dislocation glid...

Crack tip deformations and fracture parameters in functionally graded glass-filled epoxy beams are experimentally evaluated under static and dynamic loading conditions. Beams with unidirectional, monotonic elastic gradients and cracks along the gradient are examined. SEN samples with increasing or decreasing Young’s modulus ahead of the crack tip are studied in symmetric four-point bending and ...