This paper presents a low cycle fatigue life curve by simulating a crack in a cover plate welded moment connection. Initiation of ductile fracture in steel is controlled by growth and coalescence of micro-voids. This research used a numerical method using finite element modeling and simulation of ductile crack initiation by a micromechanical model. Therefore, a finite element model of a cover p...
the effect of an electroless ni-cu-p coating on the fatigue behavior of quenched and tempered ck45 steel has been investigated. the fatigue tests under rotating bending conditions have been conducted in three different conditions of uncoated, as-deposited and shot peened prior to the coating deposition. the results indicate that plating of the base steel leads to a fatigue life reduction. the d...
Fatigue crack initiation and early short crack propagation behaviour in two microstructural variants of a recently developed Low Solvus, High Refractory (LSHR) disc superalloy at room temperature has been investigated by three-point bending with replication procedure. The results shows that fine gained (FG) LSHR possesses higher fatigue life due to its better crack initiation resistance, limite...
The natural initiation and growth of short cracks in Inconel 718 U-notch specimens has been studied at 600C in air. U notches were introduced through broaching, and hardness traces and optical microscopy on cross sections through the U notch broaching showed that the broaching process had introduced a deformed, work hardened layer. Fatigue tests were conducted under load control using a 1-1-1-1...
The effect of low cycle fatigue (LCF) predamage on the subsequent very high cycle fatigue (VHCF) behavior is investigated in TC21 titanium alloy. LCF predamage is applied under 1.8% strain amplitude up to various fractions of the expected life and subsequent VHCF properties are determined using ultrasonic fatigue tests. Results show that 5% of predamage insignificantly affects the VHCF limit du...
The effect of an electroless Ni-Cu-P coating on the fatigue behavior of quenched and tempered CK45 steel has been investigated. The fatigue tests under rotating bending conditions have been conducted in three different conditions of uncoated, as-deposited and shot peened prior to the coating deposition. The results indicate that plating of the base steel leads to a fatigue life reduction. The d...
The influence of tubule orientation on the transition from fatigue to fatigue crack growth in human dentin was examined. Compact tension (CT) and rectangular beam specimens were prepared from the coronal dentin of molars with three unique tubule orientations (i.e., 0 degrees , 45 degrees and 90 degrees). The CT specimens (N=25) were used to characterize fatigue crack initiation and steady-state...
This paper proposes a reliable and cost-effective two-phase methodology to predict crack propagation life in generic two-dimensional (2D) structural components. First, the usually curved fatigue crack path and its stress-intensity factors are calculated at small crack increments in a specialized finite-element software, using automatic remeshing algorithms, special crack tip elements and approp...
Nickel-base superalloys have become the key materials of hot-end components in the aeroengines over the past several decades. Nickelbase superalloys are easy to produce thermo-mechanical fatigue (TMF) behavior when withstanding the combined effects of high temperature, creep, oxidation, mechanical stress and thermal stress. The occurrence of TMF seriously affects the normal service for hot-end ...