OBJECTIVES The purpose of this study was to evaluate flexural strengths, moduli, and maximum deflection of Clearfil AP-X (APX) and Ceram-X Mono (CXM) when cured with a quartz-tungsten halogen (QTH) or an LED-light (LED). METHODS Specimens were made according to ISO 4049 and cured with QTH or LED for 10, 20 or 60s. Flexural strength, modulus, and deflection were determined after 24 h water sto...

In the present research work, the flexural modulus and strength of glass fiber-epoxy resin and carbon fiber-epoxy resin composites have been enhanced through fiber tension during curing of the polymeric resin. This study showed that the tension applied on the fibers increased the flexural modulus of the glass-epoxy composites up to 12% and the flexural strength up to 19%. The flexural modulus a...

PURPOSE The impact strength and the flexural properties of denture base materials are of importance in predicting their clinical performance upon sudden loading. This study compares the impact and transverse strengths and the flexural modulus of three denture base polymers. MATERIALS AND METHODS The investigation included a relatively new microwave-polymerized polyurethane-based denture mater...

Surface treatment of silica fume with sulfuric acid prior to incorporation in a cement matrix resulted in composites exhibiting increases in tensile strength by 12%, tensile modulus by 72%, tensile ductility by 57%, abrasion resistance by 20%, loss tangent by 30–80%, flexural storage modulus by 80–120%, and flexural loss modulus by 160–300%, relative to the values obtained by using as-received ...

strength, flexural modulus, and contraction stress of one orthodontic composite and two flowable composites. Orthodontic brackets were bonded to 45 human maxillary premolars with the composites Transbond XT, Filtek Z-350 flow and Opallis flow and tested for shear bond strength. For measurement of flexural strength and flexural modulus, specimens were fabricated and tested under flexion. For the...

Dynamic modulus of elasticity was determined in clearwood samples of eight tropical hardwood species using longitudinal vibrations, flexural vibration and ultrasonic transit-time methods. These samples were subsequently subjected to three point static bending test to determine static modulus of elasticity and modulus of rupture. Acoustic velocity and wood density were found to be independent pa...

In the present work, Na+-montmorillonite nanoclay (Na-MMT) was functionalized using 3-aminopropyltrimethoxysilane (3-APTMS) as a coupling agent. The covalent functionalization of MMT was confirmed by Fourier-transform infrared spectroscopy (FT-IR). In the specimen fabrication stage, 5 wt% of pristine MMT or silane-functionalized MMT (f-MMT) were incorporated into an epoxy system and the resulta...

The purpose of the present study was to test the hypothesis that glazing will affect the Weibull modulus or the mean flexural strength of dental porcelain. Four groups (n = 30) of specimens were prepared from feldspathic body porcelain (Vita VMK 68). The specimens were tested in groups: original glazed condition (control), and after grinding separately with 1,000-grit, 600-grit, and 100-grit si...

The addition of different polymers, such as polytetrafluorethylene (PTFE), to denture base resins could be an option to modify acrylic resin mechanical properties. This study evaluated the surface hardness, impact and flexural strength, flexural modulus and peak load of 2 acrylic resins, one subjected to a long and another subjected to a short polymerization cycle, which were prepared with or w...

AIM The aim of this in vitro study was to compare the flexural strength, the flexural modulus and compressive strength of the acrylic polymer reinforced with glass, carbon, polyethylene and Kevlar fibres with that of plain unfilled resin. MATERIALS AND METHODS A total of 50 specimens were prepared and divided into 10 specimens each under 5 groups namely group 1- control group without any fibr...