OBJECTIVE This study determined the effects of various surface treatment modalities on the bond strength of composite resins to glass-ionomer cements. MATERIAL AND METHODS Conventional (Ketac Molar Quick Applicap) or resin-modified (Photac Fil Quick Aplicap) glass-ionomer cements were prepared. Two-step etch-rinse & bond adhesive (Adper Single Bond 2) or single-step self-etching adhesive (Adp...

The design of new synthetic grafted poly(3-hydroxybutyrate) as composite 3D-scaffolds is a convenient alternative for tissue engineering applications. The chemically modified poly(3-hydroxybutyrate) is receiving increasing attention for use as biomimetic copolymers for cell growth. As of yet, these copolymers cannot be used efficiently because of the lack of good mechanical properties. Here, we...

AIM Adhesion of composite resin and pulp capping biomaterials remarkably influences treatment outcomes. This in vitro study aimed to compare the shear bond strength of composite resin to calcium enriched mixture (CEM) cement, mineral trioxide aggregate (MTA) and resin modified glass ionomer (RMGI) with or without acid etching. MATERIALS AND METHODS A total of 90 cylindrical acrylic blocks con...

AIM The present study was conducted to determine and compare the shear bond strengths of Conventional glass ionomer; Resin-modified glass ionomer; Polyacid-modified composite and Composite Resin, and to assess and determine the mode of failure (adhesive, cohesive, mixed). MATERIALS AND METHODS Occlusal dentin of 40 extracted human teeth were randomly divided into four groups of ten teeth, eac...

AIM The purpose of this study is to evaluate the clinical performance of three different restorative materials in primary teeth according to the FDI criteria. MATERIALS AND METHODS Resin-modified glass ionomer cement, compomer and composite resin restorations (n=93) were made in 31 patients. The restorations were clinically evaluated at baseline, 6th, 12th and 18th month with the FDI criteria...

The flexural strength and flexural modulus of an experimental metal-resin composite, which used Ag-In alloy particle as the filler, were evaluated. The effect of acid treatment and heat treatment on the Ag-In alloy particle was investigated. The flexural strength of the experimental metal-resin composites ranged from 65.5 MPa to 91.0 MPa. The flexural strength of the metal-resin composite incre...

OBJECTIVE To evaluate the sealing ability of two different types of Glass Ionomer Cements (GICs) used for sandwich restorations and assess the effect of acid etching of GIC on microleakage at GIC-resin composite interface. STUDY DESIGN Experimental study. PLACE AND DURATION OF STUDY Department of Operative, DIEKIOHS (DUHS) and NED University, Karachi, from February to June 2011. METHODOLO...

The purposes of this study were to evaluate the sealing ability of different glass ionomer cements (GICs) used for sandwich restorations and to assess the effect of acid etching of GIC on microleakage at GIC-resin composite interface. Forty cavities were prepared on the proximal surfaces of 20 permanent human premolars (2 cavities per tooth), assigned to 4 groups (n=10) and restored as follows:...

Background: The clinical success of sandwich technique depends on the strength of resin-modified glass ionomer cement (RMGIC) bonding to both dentin and resin composite. Therefore, the shear bond strength (SBS) of resin composite bonded to RMGIC utilizing different resin adhesives versus a GIC-based adhesive was compared. Materials and methods: In this in vitro study, 84 holes (5×2 mm) were pre...

Resin Composites Sandwich restorations and Curing techniques Anders Lindberg, Department of Dental Hygienist Education, Faculty of Medicine, Umeå University, 901 87 Umeå, Sweden. Since the mid-1990s resin composite has been used for Class II restorations in stress-bearing areas as an alternative to amalgam. Reasons for this were the patients’ fear of mercury in dental amalgam and a growing dema...