The aim of this study was to evaluate the shear bond strength of resin composite repairs with and without aging of the surface to be repaired, using different adhesive systems and resin composites. Ninety specimens were prepared: 10 for the Control Group (GC - without repair); 40 for Group I (GI - repairs after 7 days) and 40 for Group II (GII - repairs after 180 days). Groups I and II were div...

The surface degradation of composite resins caused by accelerated aging was studied. Accelerated aging for 900 hours caused erosion of the resin matrices and exposure of filler particles. Differences in surface profiles after aging suggest that the materials eroded at different rates. Accelerated aging may model erosive wear of composites.

Composite resins were reinforced with glass and polyethylene fibers in this study, and the effect of fiber reinforcement on the color change of composite resins was investigated. After accelerated aging, the effect of fiber reinforcement on the color stability of composite resins was also examined. There were three experimental groups (n=12 disks per group): non-fiber-reinforced composite (non-...

background and aims. effect of surface treatments on repair bond strength of aged composite resins might be different due to their dissimilar fillers. the aim was to evaluate the effect of different surface treatments on repair micro-shear bond strength (µsbs) of silica- (spectrum tph) and zirconia-filled (filtek z250) composite resins. materials and methods. twenty-seven composite resin blocks...

Aim To evaluate the fracture resistance of simulated immature teeth with an apical plug of biodentine followed by composite resin vs total obturation with biodentine tested immediately and after 3 months of aging and also to find out the chemical composition of dentin in contact with these materials. Materials and methods Extracted human maxillary central incisors with simulated immature apex...

PURPOSE To explore the influence of different surface conditionings on surface changes and the influence of surface treatments and aging on the bond strengths of composites to non-aged and aged resin nanoceramics. MATERIALS AND METHODS Rectangular-shaped non-aged and aged (5000 thermocycles) resin nanoceramic specimens (Lava Ultimate) (n=63, each) were divided into 3 groups according to surfa...

The color stability of seven commercial composite resins, an unfilled resin, and three glazes was studied under conditions of accelerated aging by reflection spectrophotometry and visually with Munsell color tabs. After aging for 900 hours, most of the resins had lower values of luminous reflectance and excitation purity and higher values of dominant wavelength and contrast ratio compared to va...

The durability of resin-dentin bonds is a growing concern in the placement of composite restorations. Most reported evaluations concerning the mechanical behavior of the bonded interface are conducted using static loading to failure only. They also do not account for the acid production of biofilms, which is one of the most common contributors to interfacial failures in vivo. In this investigat...