UNLABELLED Cell culture system has been used to evaluate alloy cytotoxicity under different environments, testing the extracts, but the effect of temperature variation on the cytotoxicity of dental alloys has not been analyzed. OBJECTIVE The aim of the present study was to investigate if temperature variation could affect dental alloy cytotoxicity, testing alloy extracts in an epithelial cell...

The Ti-6Al-6Mo alloy was arc-melted eight times from pure Ti, Al, and Mo. The Ti6Al-6Mo were analyzed by using an optical microscope, SEM-EDS, XRD and Vickers Hardness Tester. Corrosion test was performed by using Hank’s solution at 37 °C and pH 7.4. The optical micrograph showed a similar structure of this alloy. The microstructure of Ti 6Al6Mo was basketweave with  lath. The map of Ti, Al an...

This study was conducted to evaluate the biocompatibility of titanium-nickel shape memory alloy used as a medical implant material. The authors carried out the following electrochemical corrosion test and in vivo and in vitro biological tests for the alloy and some metal and alloys clinically used previously to compare the intensities concerned with the biological reactions, that is, (1) anodic...

A new superelastic Ti-23Hf-3Mo-4Sn biomedical alloy displaying a particularly large recovery strain was synthesized and characterized in this study. Its native passive film is very thick (18 nm) and contains very protective TiO2, Ti2O3, HfO2, MoO2, and SnO2 oxides (XPS analysis). This alloy revealed nobler electrochemical behavior, more favorable values of the corrosion parameters and open circ...

This paper presents the wear characteristics of the composite ceramic coating made with Al2O3-40wt%8YSZ on the biomedical grade Ti-6Al-4V alloy (grade 5) used for total joint prosthetic components, with the aim of improving their tribological behavior. The coatings were deposited using a plasma spraying technique, and optimization of plasma parameters was performed using response surface method...

Metal release from implantable metals and the properties of oxide films formed on alloy surfaces were analyzed, focusing on the highly biocompatible Ti-15Zr-4Nb-4Ta alloy. The thickness and electrical resistance (Rp) of the oxide film on such an alloy were compared with those of other implantable metals. The quantity of metal released during a 1-week immersion test was considerably smaller for ...

Formation of bacterial biofilms on dental implant material surfaces (titanium) may lead to the development of peri-implant diseases influencing the long term success of dental implants. In this study, a novel Cu-bearing titanium alloy (Ti-Cu) was designed and fabricated in order to efficiently kill bacteria and discourage formation of biofilms, and then inhibit bacterial infection and prevent i...

Bending property of Ti-Ni alloy dental castings was evaluated in comparison with that of Co-Cr alloy in a cantilever test. Heat treatment effect on the bending property was also investigated in relation to phase transformation. Ti-50.85Ni (mol%) alloy was used, and the shape of bending test specimens was half-rounded in cross section, 2.0mm in diameter. The bending test was carried out at 310K....

Several formulations of alternative alloys have been proposed for the substitution of gold-based alloys used in Dentistry. Recently, a Ni-Cr-Ti-based alloy has been introduced. The purpose of this work was to verify the marginal adaptation obtained with one-piece superstructures for implant-supported prostheses obtained in Ni-Cr-Ti alloy, compared to a semi-noble alloy Pd-Ag. Eight superstructu...

PURPOSE The purpose of this study was to assess the surface characteristics and the biocompatibility of zirconium (Zr) coating on Ti-6Al-4V alloy surface by radio frequency (RF) magnetron sputtering method. MATERIALS AND METHODS The zirconium films were developed on Ti-6Al-4V discs using RF magnetron sputtering method. Surface profile, surface composition, surface roughness and surface energy...