It is well-known that some metals/alloys are sensitizing on skin contact, but it is not so well appreciated that sensitization is dependent on the reaction of the metal/alloy with sweat. The first step in skin sensitization by metals/alloys is a corrosion process and the formation of soluble metal ions. The nature of this process has implications with respect to occurrence of metal contact derm...

y-tial intermetallic alloy have a good potential for use as biomaterial, due to its good corrosion resistance. in this paper, two fundamental electrochemical techniques namely electrochemical impedance spectroscopy and potentiodynamic anodic polarization were used to evaluate the corrosion performance of g-tial in ringer's solution. surface modification treatments were employed with the pu...

Severe corrosion of epoxy coated rebar in the substructure of 5 major marine bridges in the Florida Keys was detected after only a few years of construction. Corrosion occurred underneath the coating and was preceded by loss of adherence between the steel and the coating. Damage surveys of the bridges, which were built around 1980, were conducted from 1986 to 2000. Corrosion resulted in delamin...

This short review describes various types of anti-corrosion additives of water-soluble metal working fluids for aluminum alloy materials. It is concerned with synthetic additives classified according to their functional groups; silicone compounds, carboxylic acids and dibasic acids, esters, Diels-Alder adducts, various polymers, nitrogen compounds, phosphoric esters, phosphonic acids, and other...

In china, atmospheric storage tanks are not included in the management of special equipment, and therefore they are not required to be inspected compulsorily. There is larger difference between China and developed countries on atmospheric storage tank inspection technique than the other techniques on the inspection of pressure vessels. It is widely believed that the strength worsening and perfo...

Five non-precious Ni-Co based alloys were analyzed with respect to their corrosion behaviour. The correlation between the amount of the elements Cr, Mo, V and the corrosion behaviour, expressed by the PREN (pitting resistance equivalent number) index in the case of the allied steels, was extended for Ni-Cr and Co-Cr dental alloys characterization. Open circuit potential, corrosion current densi...

The paper presents a new analytical model to study the evolution of radial cracking around a corroding steel reinforcement bar embedded in concrete. The concrete cover for the corroding rebar is modelled as a thick-walled cylinder subject to axisymmetrical displacement constraint at the internal boundary generated by expansive corrosion products. A bilinear softening curve reflecting realistic ...

The understanding of corrosion behavior in NiTi is critical for the devices using this shape-memory alloy. In order to improve the surface properties of NiTi such as corrosion resistance, plasma source ion implantation (PSII) technique was employed with oxygen as incident ions at three levels of implantation dose (5x10(16), 1x10(17) and 3x10(17) ions/cm(-2)). Pitting corrosion and wear-corrosio...

A TCP–TCL model is established to describe the relationship between the thickness of the corrosion-filled paste (CP) and that of the corrosion layer (CL). This model can describe the phenomenon that the corrosion filling in the concrete pores and accumulating at the steel/concrete interface occur synchronously. Based on the TCP–TCL model, a corrosion-induced concrete cracking model, which can q...