In the ceramic materials acoustic emission (AE) is associated with a rapid elastic energy release due to the formation and expansion of cracks, which causes generation and propagation of the elastic wave. AE pulses measurement allows monitoring of internal stresses changes and the development of macroand micro-cracks in ceramic materials, and that in turn allows us to evaluate the time to failu...

A methodology is evaluated to predict the probability of specimen failure with subsequent fatigue, after a short surface crack has been detected in Al 2219-T851 alloy. Cracks are detected and tracked to failure using optical microscopy. Predictions of remaining lifetime distributions are made with a i~onte Carlo procedure in conjunction with growth laws which model the effect of grains of diffe...

Propagation of elastic waves is studied in a 1D medium containing N cracks modeled by nonlinear jump conditions. The case N = 1 is fully understood. When N > 1, the evolution equations are written as a system of nonlinear neutral delay differential equations, leading to a well-posed Cauchy problem. In the case N = 2, some mathematical results about the existence, uniqueness and attractivity of ...

It is often postulated that quasistatic cracks propagate along the direction allowing fracture for the lowest load. Nevertheless, this statement is debated, in particular for anisotropic materials. We performed tearing experiments in anisotropic brittle thin sheets that validate this principle in the case of weak anisotropy. We also predict the existence of forbidden directions and facets in st...

Films formed through the drying of nanoparticle suspensions release the build-up of strain through a variety of different mechanisms including shear banding, crack formation and delamination. Here we show that important connections exist between these different phenomena: delamination depends on the dynamics of crack hopping, which in turn is influenced by the presence of shear bands. We also s...

INTRODUCTION Stress fractures are common in athletes, military recruits, and Thoroughbred racehorses, and may occur as hip fractures in the elderly. All of these injuries, to some extent, depend upon the propagation of fatigue cracks. Therefore, it is important to characterize the rates at which fatigue cracks grow and how microstructural differences found in cortical bone influence the crack g...

We examine the fracture mechanics of tearing graphene. We present a molecular dynamics simulation of the propagation of cracks in clamped, free-standing graphene as a function of the out-of-plane force. The geometry is motivated by experimental configurations that expose graphene sheets to out-of-plane forces, such as back-gate voltage. We establish the geometry and basic energetics of failure ...

The role of elastic mismatch in determining critical conditions for indentation fracture in brittle coatings on substrates of unlike modulus was investigated. A model transparent trilayer system, consisting of a glass coating layer bonded to a thick substrate of different glass or polymer by a thin layer of epoxy adhesive, facilitated in situ observations of crack initiation and propagation. A ...

Optimal paths play a fundamental role in numerous physical applications ranging from random polymers to brittle fracture, from the flow through porous media to information propagation. Here for the first time we explore the path that is activated once this optimal path fails and what happens when this new path also fails and so on, until the system is completely disconnected. In fact many appli...

In this article, elastic wave propagation and scattering in a solid medium permeated by uniaxially aligned penny-shaped microcracks are studied. The crack alignment refers to the case in which the unit normals of all cracks are randomly oriented within a plane of isotropy. The analysis is restricted to the limit of the noninteraction approximation among individual cracks. Explicit expressions f...