Fully reversed stress-controlled tension–compression fatigue experiments (R = −1) were conducted to study the cyclic deformation and behavior of 7075-T651 aluminum alloys with without a surface mechanical rolling treatment (SMRT). The strain amplitude, ratcheting effect, asymmetric base metal (BM) SMRT specimens analyzed. showed more remarkable effects asymmetry under high stresses. Fatigue tes...

There is an increasing need to assess the service life of components containing defect which operate at high temperature. This paper describes the current fracture mechanics concepts that are employed to predict cracking of engineering materials at high temperatures under static and cyclic loading. The relationship between these concepts and those of high temperature life assessment methods is ...

INTRODUCTION The purpose of this study was to evaluate the effect of various degrees of cyclic fatigue on torsional failure and torsional preloading on the cyclic fatigue life of heat-treated K3XF nickel-titanium (NiTi) instruments (SybronEndo, Orange, CA). METHODS The mean number of cycles until failure (Nf) of K3XF and K3 NiTi instruments was examined in a 3-point bending apparatus with a 7...

Residual compressive stress can improve fretting fatigue strength. In this paper, the effects of residual stress on fretting fatigue of Al 2024-T351 alloy specimens are studied using a numerical approach. The extended finite element method combined with the cyclic cohesive zone model is adopted to model fretting fatigue crack growth behavior. It is shown that residual stress changes the frettin...

Artificial Neural Networks (ANN) have recently been used in modeling the mechanical behavior of fiber-reinforced composite materials. The use of ANN in predicting fatigue failure in composites would be of great value if one could predict the failure of materials other than those used for training the network. This would allow developers of new materials to estimate in advance the fatigue proper...

Fretting fatigue induced by combined localized cyclic contact motion and external bulk fatigue loadings may result in premature and dramatic failure of the contacting components. Depending on fretting and fatigue loading conditions, crack nucleation and possibly crack propagation can be activated. This paper proposes a procedure for estimating these two damage thresholds. The crack nucleation b...

Fretting fatigue induced by combined localized cyclic contact motion and external bulk fatigue loadings may result in premature and dramatic failure of the contacting components. Depending on fretting and fatigue loading conditions, crack nucleation and possibly crack propagation can be activated. This paper proposes a procedure for estimating these two damage thresholds. The crack nucleation b...

Effect of holding time and temperature on the fatigue life of micro Sn-Ag-Cu solder joint has been studied with waveform of triangle and trapezoid wave at 298K and 398K. Both the microstructural coarsening and the crack propagation occurred simultaneously and therefore the cyclic load decreased rapidly in the trapezoidal wave at 398K compared with the other conditions. Therefore, under the cond...

The aim of the present research is to investigate the fatigue behaviour of friction stir (FS) welded tubular joints in aluminium alloy subjected to torsional fatigue loading. To manufacture the samples which were tested, an MTS I-STIR process development system was equipped with a retracting tool specifically designed for these tubular welds. Al 6082-T6 FS welded samples were tested under cycli...

In this paper, a Paris law-based model is presented whereby crack propagation occurs under cyclic loading in air (fatigue) and in an aggressive environment (corrosion-fatigue) for the case of corner cracks (with a wide range of aspect ratios in the matter of the initial cracks) in finite-thickness plates of 316L austenitic stainless steel subjected to tension, bending, or combined (tension + be...