Cobalt-doped tungsten disulfide nanorods were synthesized by an approach involving exfoliation, intercalation, and the hydrothermal process, using commercial WS2 powder as the precursor and n-butyllithium as the exfoliating reagent. XRD results indicate that the crystal phase of the sample is 2H-WS2. TEM images show that the sample consists of bamboo-like nanorods with a diameter of around 20 n...

We prepared rod-shaped gold nanorattles solid gold nanorods surrounded by a thin gold shell using a galvanic replacement process starting with silver-coated gold nanorods. These structures are very promising candidates for catalytic applications and optimized plasmon sensors. They combine the advantages of rods (low plasmon resonance frequency, large polarizability, small damping) with the high...

ZnO nanorods were grown on a silver-coated tip of a borosilicate glass capillary (0.7 μm in tip diameter) and used as selective potentiometric sensor of intracellular free Mg(2+). To functionalize the ZnO nanorods for selectivity of Mg(2+), a polymeric membrane with Mg(2+)-selective ionophores were coated on the surface of the ZnO nanorods. These functionalized ZnO nanorods exhibited a Mg(2+)-d...

Well-dispersed barium borate nanorods with uniform diameters were synthesized successfully, using Na2B4O7 x 10H2O and Ba(NO3)2 as raw materials and oleic acid as a modifying agent. Oleic acid was used to modify the surface property of nanorods prepared from the precipitation reaction. TEM images confirmed that the synthesized sample presented nanorod morphology with a length of about 200-400 nm...

ZnO thin films with grain morphology were obtained over glass substrates using the sol–gel method; these films were used as substrates to grow ZnO nanorods using chemical bath deposition (CBD) technique. The transmittance percentage of two films was over 85% and the electrical resistivity decreased when ZnO nanorods were grown over the ZnO thin film with grain morphology. A laser is incident at...

In the present work, novel nanotool called 'nano-embedded fungus' formed by impact of synergistic association of ZnO-nanorods and fungus Piriformospora indica DSM 11827, for growth of Brassica oleracea var. botrytis (Broccoli) is reported. ZnO-nanorods were synthesized by mechanical assisted thermal decomposition process and characterized by scanning electron microscopy (SEM) for morphology, X-...

Several important synthetic parameters such as precursor concentration, rate of evaporation and reaction time are found to determine the growth of ZnO nanostructures. These reaction parameters can be tailored and tuned to produce a variety of nanostructures ranging from nanoparticles, nanorods and nanospheres. The nanorods are structurally uniform made up of crystallographically oriented attach...

We report observation of catalyst-free hydride vapor phase epitaxy growth of InN nanorods. Characterization of the nanorods with transmission electron microscopy, and X-ray diffraction show that the nanorods are stoichiometric 2H-InN single crystals growing in the [0001] orientation. The InN rods are uniform, showing very little variation in both diameter and length. Surprisingly, the rods show...

Direct measurements of carrier diffusion in GaN nanorods with a designed InGaN/GaN layer-in-a-wire structure by scanning near-field optical microscopy (SNOM) were performed at liquid-helium temperatures of 10 K. Without an applied voltage, intrinsic diffusion lengths of photo-excited carriers were measured as the diameters of the nanorods differ from 50 to 800 nm. The critical diameter of nanor...

The orientation-dependent structural properties of Zn(1-x)Mg(x)O nanorods with different Mg concentrations were investigated quantitatively using polarization-dependent extended X-ray absorption fine structure (EXAFS) measurements at the Zn K edge. Vertically-aligned Zn(1-x)Mg(x)O nanorods were synthesized on Si substrates using catalyst free metal organic chemical vapor deposition. Polarizatio...