Flexible composite films were produced by impregnating aqueous phenol formaldehyde (PF) resin into water-swollen cellulose nanofibril (CNF) films. CNF films were prepared using a pressurized filtration method in combination with freeze drying. The freeze-dried films were swollen with water then impregnated with PF resin by soaking in aqueous resin solutions of varying concentrations. Small amou...

In this study, a green composite was produced from Oil Palm Trunk Lumber (OPTL) by impregnating oil palm shell (OPS) nanoparticles with formaldehyde resin. The changes of physical, mechanical and morphological properties of the OPS nanoparticles impregnated OPTL as a result of natural weathering was investigated. The OPS fibres were ground with a ball-mill for producing nanoparticles before bei...

Dendrocalamus latiflorus Munro (ma bamboo) was liquefied in phenol or in polyethylene glycol/glycerol cosolvent, with H2SO4 as a catalyst. The liquefied bamboo was reacted with bisphenol-A and epichlorohydrin to prepare copolymer epoxy resins. The thermal properties of resins during and after curing were investigated by differential scanning calorimetry (DSC) and dynamic mechanical analysis (DM...

The objective of this research was to provide a useful approach of polymer synthesis for accelerating the fast cure of phenol-urea-formaldehyde (PUF) resin as wood adhesive by optimizing its structure and composition. The PUF resins containing high contents of very reactive groups such as para-methylol groups were synthesized by reacting methylolurea, phenol, and formaldehyde in the presence of...

TG-FTIR and PY-GC/MS were used to analyze the pyrolysis behaviors of pine wood, urea-formaldehyde resin (UF resin) their blended pellets. The process was divided into three stages: water evaporation, devolatilization residue decomposition. During pellets, with increase addition ratio UF resin, peak value weight loss decreased in decomposition stage residue, while temperature shifted low-tempera...

Three types of adhesives, urea-formaldehyde (UF) resin, phenol-formaldehyde (PF) resin, and polymeric methylene bis(phenyl isocyanate) (pMDI), were used for investigating the effect of pressing variables on volatile organic compound (VOC) emissions. The variables examined included press temperature and time, mat moisture content and resin content, and board density. The VOCs emitted during part...

Compression molded composites were made from wood particles and a liquefied wood/phenol/formaldehyde co-condensed resin. Based on our previous research, a phenol to wood (P1W) ratio of 2/1 was chosen for this study. The two experimental variables selected were: 1) liquefaction temperature (1500 and 180°C) and 2) cooking method (atmospheric and sealed). Panels were tested in static bending for m...

In this work two types of lignin-novolac resins have been formulated, partially substituting phenol by softwood ammonium lignosulfonate as filler or extender (methylolated) to study the viability of that substitution when resins will be employed as adhesives in textile felts. A commercial novolac resin was used as reference. Free phenol, free formaldehyde, water content, softening point, and fl...