Simultaneous measurements of the curves for wear versus distance, wear rate versus distance, and coefficient of friction versus distance were performed in situ to distinguish the transition from severe running-in wear to mild wear. The effects of the initial surface roughness on the severe running-in wear volume were investigated. Disk-on-plate friction and wear tests were carried out with SUS3...

The microstructures and weldability of a brazed joint of 1Cr18Ni9Ti austenitic stainless steel with BNi-2, BNi82CrSiBFe and BMn50NiCuCrCo filler metals in vacuum were investigated. It can be observed that an interdiffusion region existed between the filler metal and the base metal for the brazed joint of Ni-based filler metals. The width of the interdiffusion region was about 10 μm, and the mic...

AE monitoring from various types of stress corrosion cracking (SCC) has been conducted for the past 15 years in our laboratory. This paper discusses AE results of active-path dissolution-type SCC of austenitic stainless steel in chloride solution and fused salt, fluoride and polythionic acid solutions, brass in ammonia (Mattosson's solution), and carbon steels in nitrite solution. Transgranular...

Austenitic carbon steels that exhibit excellent mechanical properties due to the twinning-induced plasticity effect have been studied extensively. On the other hand, austenitic stainless steels usually achieve good strength and ductility via transformation-induced plasticity. However, relying on martensite transformation for strength may cause problems such as delayed cracking. Therefore, the t...

Complex two-component peak of anelastic mechanical losses was observed in multicomponent substitutional austenitic alloys after prior plastic deformation. In AISI 316L, AISI 316LN, AISI 310 and AISI 304 austenitic stainless steels, this peak is situated in the wide range of temperature from 200 to 400K. Characteristics of the observed peak for different thermo-mechanical treatments were studied...

Intergranular stress corrosion cracking has occurred in BWR environments in non-sensitised, cold-worked austenitic stainless steel materials. The affecting parameters are so far not fully known, but deformation mechanisms may be decisive. The effect of cold deformation and nitrogen content on the deformation behaviour of austenitic stainless steels was investigated. The materials were austeniti...

In the present study, the Weldability and microstructure of dissimilar welds of AISI 347austenitic stainless steel to ASTM A335 low alloy steel was investigated. For this purpose, gas tungsten arc welding process and two filler metals including ERNICr-3 and ER309L were used. After welding, the microstructure of the different zones of each joint, including weld metals, heat affected zone (HAZ) 1...

Stainless steel has been employed in many engineering applications ranging from pharmaceutical equipment to piping in the nuclear reactors and storage to chemical products. In this attempt, simulation of fatigue crack growth based on experimental results of austenitic stainless steel 304L was presented using AFGROW code when NASGRO mode laws adopted. Double through crack at hole specimen is use...

in the present study, the microstructure and mechanical properties of the dissimilar welding betweenastm a335 low alloy steel and er309l austenitic stainless steel were investigated using the gastungsten arc welding process. the welding of dissimilar materials between astm a335 low alloy steeland er309l austenitic stainless steel was found to have a significant effect on the microstructure when...

In the present study, the microstructure and mechanical properties of the dissimilar welding between ASTM A335 low alloy steel and ER309L austenitic stainless steel were investigated using the gas tungsten arc welding process. The welding of dissimilar materials between ASTM A335 low alloy steel and ER309L austenitic stainless steel was found to have a significant effect on the microstructure w...