Non-corrosive, carbon-based materials are usually used as anodes in microbial fuel cells (MFCs). In some cases, however, metals have been used that can corrode (e.g. copper) or that are corrosion resistant (e.g. stainless steel, SS). Corrosion could increase current through galvanic (abiotic) current production or by increasing exposed surface area, or decrease current due to generation of toxi...

Previous studies showed that temperature and total organic carbon in drinking water would cause chlorine dioxide (ClO(2)) loss in a water distribution system and affect the efficiency of ClO(2) for Legionella control. However, among the various causes of ClO(2) loss in a drinking water distribution system, the loss of disinfectant due to the reaction with corrosion scales has not been studied i...

The ions released from conventional and high-copper amalgams in contact with titanium were quantitatively analyzed in a 0.9% NaCl solution at 37 degrees C when the surface area ratio of titanium/amalgam was set up as 1/10, 1/1, or 10/1. The corrosion potentials of the amalgams and titanium were measured under the same conditions. Surface analyses on the amalgams were also employed using SEM wit...

Results from the international cooperative programme on effects on materials including historic and cultural monuments are presented from the period 1987-2014 and include pollution data (SO₂, NO₂, O₃, HNO₃ and PM10), corrosion data (carbon steel, weathering steel, zinc, copper, aluminium and limestone) and data on the soiling of modern glass for nineteen industrial, urban and rural test sites i...

A method for the detection of in situ corrosion monitoring due to atmospheric gasses has been incorporated to measure not only the amount of corrosion on a copper surface but also the rate of corrosion and a study on the bonding of the adsorbent at the gas solid interface. The Quartz Crystal Microbalance (QCM) has recently been used for this corrosion monitoring. Results indicate a difference i...

In this study, corrosion behavior of copper that was deformed by Simple Shear Extrusion (SSE) method was investigated in 3%wt NaCl solution. Modified Williamson-Hall method, applied on the X-ray diffraction patterns of the samples, showed that increase in the number of SSE passes led to increasing in the dislocation density in the copper samples. Moreover, such deformed samples exh...

This article reports an experimental and theoretical investigation of mercury dissolution from dental amalgams immersed in neutral (noncorrosive) and acidic (corrosive) flows. Atomic absorption spectrophotometric measurements of Hg loss indicate that in neutral flow, surface oxide films formed in air prior to immersion persist and effectively suppress significant mercury release. In acidic (pH ...

The corrosion behavior of copper cold spray coatings on a carbon steel substrate was compared to that of commercially available wrought copper under the conditions anticipated in a nuclear waste repository. Corrosion potential and linear polarization resistance measurements were conducted over 90 d to 120 d in 3.0 mol/L NaCl under anoxic (1) and oxygenated-toanoxic (2) conditions to simulate th...

Dip-coated polystyrene layers of sub-micrometre thickness (85-500nm) have been applied on copper and copper alloys (aluminium brass, copper-nickel 70/30), as well as on stainless steel 304, and produced an effective barrier against corrosion and adhesion of corrosion-relevant microorganisms. According to the dynamic wettability measurements, the coatings exhibited high advancing (103°), recedin...

To solve the main problems of existing coarse grained copper (CG Cu) intrauterine devices (IUD)-namely burst release and a low transfer efficiency of the cupric ions during usage-ultra-fine grained copper (UFG Cu) and single crystal copper (SC Cu) have been investigated as potential substitutes. Their corrosion properties with CG Cu as a control have been studied in simulated uterine fluid (SUF...