The natural initiation and growth of short cracks in Inconel 718 U-notch specimens has been studied at 600C in air. U notches were introduced through broaching, and hardness traces and optical microscopy on cross sections through the U notch broaching showed that the broaching process had introduced a deformed, work hardened layer. Fatigue tests were conducted under load control using a 1-1-1-1...

The objective of this investigation was to develop an innovative methodology for life and reliability prediction of hot-section components in advanced turbopropulsion systems. A set of generic microstructure-based time-dependent crack growth (TDCG) models was developed and used to assess the sources of material variability due to microstructure and material parameters such as grain size, activa...

Self-healing polymers, based on microencapsulated dicyclopentadiene and Grubbs' catalyst embedded in the polymer matrix, are capable of responding to propagating fatigue cracks by autonomic processes that lead to higher endurance limits and life extension, or even the complete arrest of the crack growth. The amount of fatigue-life extension depends on the relative magnitude of the mechanical ki...

The evaluation of energy release rate and centre Crack Opening Displacement (COD) for circumferential Through-Wall Cracked (TWC) pipes is an important issue in the assessment of critical crack length for unstable fracture. The ability to predict crack growth continues to be an important component of research for several structural materials. Crack growth predictions can aid the understanding of...

Understanding the fatigue crack growth phenomenon in railheads requires a study of driving forces such as the crack tip opening and sliding displacements, under repeated rolling contact. Finite element simulations, allowing elastic-plastic deformation, and mixed-mode crack growth laws were utilized to demonstrate that the fatigue crack growth rates display a minimum after a finite amount of cra...

Stainless steel has been employed in many engineering applications ranging from pharmaceutical equipment to piping in the nuclear reactors and storage to chemical products. In this attempt, simulation of fatigue crack growth based on experimental results of austenitic stainless steel 304L was presented using AFGROW code when NASGRO mode laws adopted. Double through crack at hole specimen is use...

Stainless steel has been employed in many engineering applications ranging from pharmaceutical equipment to piping in the nuclear reactors and storage to chemical products. In this attempt, simulation of fatigue crack growth based on experimental results of austenitic stainless steel 304L was presented using AFGROW code when NASGRO mode laws adopted. Double through crack at hole specimen is use...

The unexpected failures of structural materials in very high cycle fatigue (VHCF) regime have been a critical issue in modern engineering design. In this study, the VHCF property of a Cr-Ni-W gear steel was experimentally investigated under axial loading with the stress ratio of R = -1, and a life prediction model associated with crack initiation and growth behaviors was proposed. Results show ...

In the present investigation, an attempt has been made to use “exponential model” in the prediction of fatigue life without integrating the fatigue crack growth rate curve (FCGR). The obtained results are compared with experimental crack growth data obtained for 2024-T351 aluminum alloy for four bending V-Charpy specimens under constant amplitude loading in stress ratio range from 0.1 to 0.3 an...