In this work, the mechanism for fracture of brittle substances such as rocks under a uniform normal tension is considered. The oriented straight micro-cracks are mostly created in all the polycrystalline materials resulting from the stress concentrations. The present work focuses on the interactions of the pre-existing micro-cracks, which can grow and propagate within a rock-like specimen. The ...

Based on the existing research results, a theoretical fracture model of strata under compound impact static and harmonic dynamic load is improved, characteristic parameters (stress intensity factor, T-stress, initiation angle) two far-field stress are determined according to crack dip angle. Additionally, effects distribution field (the angle, degree, number units, area) further calculated disc...

This study aims at determining the critical seismic intensity at which cracks are expected to develop in a concrete arch dam. This intensity is referred to as crack initiation intensity. The crack initiation intensity measure implies that earthquakes with the intensity measure higher than this value are expected to induce cracks in the arch dam. This quantity is an indicator for seismic evaluat...

The experimentally determined marked rise of the stress intensity factor required to initiate crack propagation in brittle solids under variably high loading rates, is analyzed. This problem of fracture initiation at the tip of a crack is considered in terms of activating a flaw at some distance away from the tip. By using a semi-infinite crack in an unbounded two-dimensional solid subjected to...

In this paper, we construct a model for prediction of fatigue crack initiation based on the material’s microstructure. In order to do so, the energy of a persistent slip band (PSB) is monitored and an energy balance approach is taken, in which cracks initiate and the material fails due to stress concentration from a PSB (with respect to dislocation motion). These PSBs are able to traverse low-a...

In the study of pre-fabricated single-fissured rock, failure mode, mechanical properties and propagation law rock are affected by length inclination angle fissure. this study, artificially prepared marble-like rocks with different fissure characteristics were used as representatives, using PFC 2D software to establish a uniaxial compression model tests for fissures. The effects lengths angles o...

Converting chemical energy into electricity is done by an electro-chemical device known as a fuel cell. Thermal stress is caused at high operating temperature between 700 oC to 1000 oC of SOFC. Thermal stress causes gas escape, structure variability, crack initiation, crack propagation, and cease operation of the SOFC before its lifetime. The aim of this study is to presen...

Attached ultrasonic sensors can detect changes caused by crack initiation and growth if the wave path is directed through the area of critical crack formation. Dynamics of cracks opening and closing under load cause nonlinear modulation of received ultrasonic signals, enabling small cracks to be detected by stationary sensors. A methodology is presented based upon the behavior of ultrasonic sig...

In this study, the pitting type of corrosion growth characteristics, fatigue crack initiation and propagation behavior; axial fatigue tests were carried out on precipitation hardened martensitic Custom 450 steel in the air and 3.5wt% NaCl solution. Using the ratio of the depth to the half-width of the pits; (a/c)= 1.5±0.2 the corrosion pit depth growth law was obtained as a function of stress a...

An observed minimum in the critical crack initiation load at Poisson’s ratio (ν) of 0.21–0.22 in Na2O–TiO2–SiO2 glasses was investigated. Vickers indentation was used to examine hardness and average cracking length, fracture toughness was measured through the single-edge pre-cracked beam method, and volumes of densification and shear flow around indents were measured using atomic force microsco...